Branched poly(hydroxyalkanoate) polymer salt electrolytic compositions and method of preparation

Assignee: UNIV MICHIGAN STATEPriority: Dec 21, 1992Filed: Mar 21, 1994Granted: May 28, 1996

Est. expiryDec 21, 2012(expired)· nominal 20-yr term from priority

Inventors:Rosetta N. Reusch William H. Reusch

H01M 6/181C08K 3/16H01B 1/122C08L 67/04

PatentIndex Score

Cited by

References

Claims

Abstract

Compositions and method for providing a solid conductive electrolyte composition containing a .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.(PHA) and a salt of a conductive metal are described. The PHA is a biodegradable and biocompatible and provides a basis for batteries which are more environmentally degradable. Naturally occurring polymers including polyhydroxybutyrate (PHB) and polyhydroxyvalerate (PHV) can be used to prepare the compositions.

Claims

exact text as granted — not AI-modified

We claim:

1. A solid conductive electrolyte composition which comprises in admixture: (a) a .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer having repeating units selected from the group consisting of the formula: ##STR3## wherein R is selected from the group consisting of a lower alkyl and a lower alkenyl containing 1 to 10 carbon atoms and n is a number which produces a molecular weight between about 10 4 and 10 6 ; and (b) a salt of a conductive metal, wherein the mole ratio of polymer to salt is between about 20 to 1 and 5 to 1.

2. The composition of claim 1 wherein R is both methyl and ethyl groups.

3. The composition of any one of claims 1 or 2 wherein the metal is lithium.

4. The composition of claim 1 including a plasticizer for the polymer in the composition in a mole ratio of polymer to plasticizer of between about 10 to 1 and 2 to 1.

5. The composition of claim 1 including a polyalkylene oxide polymer selected from the group consisting of polyethylene oxide and polypropylene oxide in a mole ratio of .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.to polyoxyalkylene oxide polymer between about 100 to 1 and 1 to 100.

6. The composition of claim 1 wherein the composition contains 85 to 95 mole percent of the .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer and 5 to 15 mole percent of the salt.

7. The composition of claim 6 wherein R is selected from the group consisting of methyl, ethyl and mixtures thereof.

8. The composition of claim 7 wherein the metal is lithium.

9. The composition of claim 4 wherein the composition contains 65 to 85 mole percent of the .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer, 5 to 15 mole percent of the salt and 10 to 30 mole percent of the plasticizer.

10. The composition of claim 9 wherein R is selected from the group consisting of methyl, ethyl and mixtures thereof.

11. The composition of claim 10 wherein the metal is lithium.

12. The composition of claim 5 wherein the .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.is between 40 to 85 mole percent, the salt is between 5 to 15 mole percent and polyalkylene oxide is between about 10 and 45 mole percent.

13. The composition of claim 12 wherein R is selected from the group consisting of methyl, ethyl and mixtures thereof.

14. The composition of claim 13 wherein the metal is lithium.

15. The composition of claim 1 wherein the polymer has been transesterified with an alpha, omega diol containing 2 to 10 carbon atoms.

16. The composition of claim 15 wherein the diol is selected from the group consisting of triethylene glycol and tetraethylene glycol.

17. In a method for providing a solid conductive electrolyte composition .[.has.]. .Iadd.as .Iaddend.a conductor, the improvement which comprises providing a .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer having repeating units selected from the group consisting of the formula: ##STR4## in admixture with a salt, where R is a lower alkyl and a lower alkenyl containing 1 to 10 carbon atoms and n is a number which produces a molecular weight between about 10 4 and 10 6 .

18. The method of claim 17 wherein R is both methyl and ethyl groups.

19. The method of any one of claims 17 or 18 wherein the metal is lithium.

20. The method of claim 17 including a plasticizer for the polymer in the composition in a mole ratio of polymer to plasticizer of between about 10 to 1 and 2 to 1.

21. The method of claim 17 including a polyalkylene oxide polymer in the composition selected from the group consisting of polyethylene oxide and polypropylene oxide in a mole ratio of .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer to polyoxyalkylene oxide polymer between about 100 to 1 and 1 to 100.

22. The method of claim 17 wherein the composition contains 85 to 95 mole percent of the .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer and 5 to 15 mole percent of the salt.

23. The method of claim 17 wherein R is selected from the group consisting of methyl, ethyl and mixtures thereof.

24. The method of claim 23 wherein the metal is lithium.

25. The method of claim 17 wherein the composition contains 65 to 85 mole percent of the .[.polyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer, 5 to 15 percent of the salt and 10 to 30 mole percent of the plasticizer.

26. The method of claim 17 wherein R is selected from the group consisting of methyl, ethyl and mixtures thereof.

27. The method of claim 26 wherein the metal is lithium.

28. The method of claim 17 wherein the .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.is between 40 to 85 mole percent, the salt is between 5 to 15 mole percent and the polyalkylene oxide is between about 10 and 45 mole percent.

29. The method of claim 17 wherein R is selected from the group consisting of methyl, ethyl and mixtures thereof.

30. The method of claim 29 wherein the metal is lithium.

31. The method of claim 17 wherein the polymer has been transesterified with an alpha, omega diol containing 2 to 10 carbon atoms.

32. The method of claim 31 wherein the diol is selected from the group consisting of triethylene glycol and tetraethylene glycol.

33. In a battery including a thin film of an electrolyte composition between an anode and a cathode the improvement which comprises a solid conductive electrolyte composition which comprises in admixture: (a) a .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer having repeating units selected from the group consisting of the formula: ##STR5## wherein R is selected from the group consisting of a lower alkyl and a lower alkenyl containing 1 to 10 carbon atoms and n is a number which produces a molecular weight between about 10 4 and 10 6 ; and (b) a salt of a conductive metal, wherein the mole ratio of polymer to salt is between about 20 to 1 and 5 to 1.

34. The battery of claim 33 wherein R is both methyl and ethyl group.

35. The battery of claim 33 or 34 wherein the metal is lithium.

36. The battery of claim 33 wherein the composition includes a plasticizer for the polymer in the composition in a mole .[.ration.]. .Iadd.ratio .Iaddend.of polymer to plasticizer of between about 10 to 1 and 2 to 1.

37. The battery of claim 33 wherein the composition includes a polyalkylene oxide polymer selected from the group consisting of polyethylene oxide and polypropylene oxide in a mole ratio of .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.to polyoxyalkylene oxide polymer between about 100 to 1 and 1 to 100.

38. The battery of claim 33 wherein the .[.polyhydroxyalkanoate.]. .Iadd.poly(hydroxyalkanoate) .Iaddend.polymer is naturally occurring.