Metal oxides-silica composite and method for preparing the same

Abstract

Metal oxides-silica composite materials are synthesized by a co-precipitation method to serve as modified catalysts for converting ethanol into four-carbon hydrocarbons. The method includes mixing a liquid-phase silicon source and a metal precursor at different ratios so as to change the acid-base composition of the composite materials and thereby increase selectivity with respect to the four-carbon products.

What is claimed is: 
     
         1 . A method for preparing a metal oxides-silica composite, comprising the steps of:
 titrating a basic solution with a metal precursor solution so that a titration reaction takes place between the metal precursor solution and the basic solution at a pH value greater than 7, wherein the basic solution contains a basic agent dissolved in a first solvent, the metal precursor solution contains an M 3+  salt and an N 2+  salt, both dissolved in a second solvent, and the M 3+  salt and the N 2+  salt are a trivalent metal salt and a bivalent metal salt respectively, with an N:M molar ratio of 3:1;   adding a liquid-phase silicon source after completion of the titration reaction, and then allowing an aging reaction to take place, thereby obtaining a precipitate, wherein the liquid-phase silicon source is added at an N 2+ :M 3+ :Si molar ratio of 3:1:x, in which 0<x≤10; and   calcinating the precipitate to obtain the metal oxides-silica composite.   
     
     
         2 . The method of  claim 1 , wherein the M 3+  salt is an aluminum salt, and the N 2+  salt is a magnesium salt. 
     
     
         3 . The method of  claim 2 , wherein the M 3+  salt is aluminum nitrate, and the N 2+  salt is magnesium nitrate. 
     
     
         4 . The method of  claim 1 , wherein the basic agent is an alkali metal hydroxide. 
     
     
         5 . The method of  claim 1 , wherein both the first solvent and the second solvent are water or aqueous alcohol solutions. 
     
     
         6 . The method of  claim 1 , wherein the liquid-phase silicon source is selected from the group consisting of alkoxysilane, silicate, and a combination thereof. 
     
     
         7 . The method of  claim 1 , wherein the titration reaction takes place at a pH value greater than or equal to 10. 
     
     
         8 . The method of  claim 1 , wherein the calcinating is performed at a temperature of at least 100° C. 
     
     
         9 . The method of  claim 8 , wherein the calcinating comprises: performing a first calcination process at least 110° C. for a first predetermined amount of time, then raising to at least 550° C. at which performs a second calcination process for a second predetermined amount of time. 
     
     
         10 . The method of  claim 9 , wherein the first predetermined amount of time is at least 6 hours, and the second predetermined amount of time is at least 12 hours. 
     
     
         11 . The method of  claim 1 , wherein the calcinating is performed after the precipitate is dried.