Ultra low thermo fusion pvc alternative plastisol coating and textile printing ink

Abstract

The present invention relates to a novel PVC-free plastisol composition that cures at a temperature much lower than conventional plastisols. Also disclosed is a method of applying the composition.

1 . A plastisol composition comprising:
 (a) an acrylate polymer; and   (b) a plasticizer mixture comprising at least three plasticizers selected from the group consisting of 2,2,4-trimethyl-1,3 pentanediol diisobutyrate, dioctyl terephthalate, dibutyl terephthalate, and benzyl butyl 1,2-cyclohexyldicarboxylate.   
     
     
         2 . The plastisol composition of  claim 1 , wherein the ratio between the total weight of the plasticizers and the weight of the acrylate polymer ranges from about 5:10 to about 10:10. 
     
     
         3 . The plastisol composition of  claim 1 , wherein more than about 80% of the acrylate polymer is methacrylate polymer. 
     
     
         4 . The plastisol composition of  claim 1 , wherein the mean particle size of the acrylate polymer is less than about 0.060 mm. 
     
     
         5 . The plastisol composition of  claim 1 , wherein the mean particle size of the acrylate polymer is about 0.045 mm. 
     
     
         6 . The plastisol composition of  claim 1 , wherein the plasticizer mixture comprises 2,2,4-trimethyl-1,3 pentanediol diisobutyrate, and the ratio between the 2,2,4-trimethyl-1,3 pentanediol diisobutyrate and the acrylate polymer ranges from about 1:200 and 1:10 by weight. 
     
     
         7 . The plastisol composition of  claim 1 , wherein the plasticizer comprises dioctyl terephthalate, and the ratio between the dioctyl terephthalate and the acrylate polymer ranges from about 1:10 and 1:3 by weight. 
     
     
         8 . The plastisol composition of  claim 1 , wherein the plasticizer comprises benzyl butyl 1,2-cyclohexyldicarboxylate, and the ratio between the benzyl butyl 1,2-cyclohexyldicarboxylate and the acrylate polymer ranges from about 1:10 and 1:6 by weight. 
     
     
         9 . The plastisol composition of  claim 1 , wherein the plasticizer comprises dibutyl terephthalate, and the ratio between the dibutyl terephthalate and the acrylate polymer ranges from about 1:4 and 1:2 by weight. 
     
     
         10 . The plastisol composition of  claim 1 , further comprising at least one ingredient selected from the group consisting of a wetting agent, a dispersing agent, a cross-linking agent, a filler, a blowing agent, a rheology modifier, a thixotropic agent, a lubricant, an anti-static agent, a heat stabilizer, a pigment, a flame retardant, a foaming agent, a viscosity reducer, a dilatancy reducer, and an UV absorber. 
     
     
         11 . The plastisol composition of  claim 10 , wherein the wetting agent and/or dispersing agent is selected from the group consisting of an alkoxylate, a polar acidic ester, an anionic electrolyte, an acidic polyether, polydimethylsiloxane, a fluoro-substituted polyacrylate, and any combination thereof. 
     
     
         12 . The plastisol composition of  claim 10 , wherein the crosslinking agent is selected from the group consisting of a peroxide, a tri-acrylate, and any combination thereof. 
     
     
         13 . The plastisol composition of  claim 10 , wherein the filler is selected from the group consisting of calcium carbonate, alumina trihydrate, micro sphere, silica, nepheline syenite, and any combination thereof. 
     
     
         14 . The plastisol composition of  claim 10 , wherein the blowing agent is selected from the group consisting of an expandable microsphere, a copolymer of acrylate, and a combination thereof. 
     
     
         15 . The plastisol composition of  claim 10 , wherein the rheology modifier and/or a thixotropic agent is silica. 
     
     
         16 . The plastisol composition of  claim 10 , wherein the lubricant is selected from the group consisting of paraffin wax, polytetrafluoroethlene, and a combination thereof. 
     
     
         17 . The plastisol composition of  claim 10 , wherein the anti-static agent is selected from the group consisting of an alkoxy titanate, an ammonium salt, and a combination thereof. 
     
     
         18 . A method of using the plastisol composition of  claim 1 , comprising:
 (a) applying the plastisol composition to a substrate; and   (b) exposing plastisol composition to a UV or heat source to cure the composition.   
     
     
         19 . The method of  claim 18 , wherein the plastisol composition is exposed to the heat source at a temperature of lower than about 150° C. 
     
     
         20 . (canceled) 
     
     
         21 . The method of  claim 18 , wherein the plastisol composition is exposed to the heat source for less than about 10 seconds. 
     
     
         22 - 25 . (canceled)