Separation of gases via carbonized vinylidene chloride copolymer gas separation membranes and processes therefore

Abstract

A carbonized PVDC copolymer useful for the separation of an olefin from its corresponding paraffin may be made by heating a polyvinylidene chloride copolymer film or hollow fiber having a thickness of 1 micrometer to 20 micrometers to a pretreatment temperature of 100° C. to 180° C. to form a pretreated polyvinylidene chloride copolymer film and then heating the pretreated polyvinylidene chloride copolymer film to a maximum pyrolysis temperature from 350° C. to 750° C. A process for separating an olefin from its corresponding paraffin in a gas mixture is comprised of flowing the gas mixture through the aforementioned carbonized polyvinylidene chloride (PVDC) copolymer to produce a permeate first stream having an increased concentration of the olefin and a second retentate stream having an increased concentration of its corresponding paraffin.

1 .- 12 . (canceled) 
     
     
         13 . A method of making a carbonized polyvinylidene chloride copolymer useful to separate an olefin from its corresponding paraffin comprising,
 (a) providing a polyvinylidene chloride copolymer film or hollow fiber having a thickness of 1 micrometer to 20 micrometers,   (b) heating the polyvinylidene chloride copolymer film or hollow fiber to a pretreatment temperature of 100° C. to 180° C. while restraining the polyvinylidene chloride copolymer film or hollow fiber by applying a force to form a pretreated polyvinylidene chloride copolymer film or hollow fiber, and   (c) heating the pretreated polyvinylidene chloride copolymer film or hollow fiber to a maximum pyrolysis temperature from 350° C. to 750° C. while restraining the pretreated polyvinylidene chloride copolymer film or hollow fiber by applying a force.   
     
     
         14 . The method of  claim 13 , wherein the maximum pyrolysis temperature is at most 650° C. 
     
     
         15 . The method of  claim 13 , wherein the polyvinylidene chloride copolymer film or hollow fiber is a polyvinylidene chloride copolymer comprised of vinylidene chloride and at least one of the following: a vinyl monomer; a vinyl chloride monomer; an acrylate monomer; a methacrylate monomer; a styrenic monomer; acrylonitrile, methacrylonitrile; itaconic acid; chlorotrifluoroethylene that have been copolymerized. 
     
     
         16 . The method of  claim 13 , wherein the thickness is from 1 micrometers to 10 micrometers. 
     
     
         17 . The method of  claim 13 , wherein the polyvinylidene chloride copolymer film or hollow fiber is formed by melt-extrusion at a stretch ratio from 1 to 8. 
     
     
         18 . The process of  claim 13 , wherein the polyvinylidene chloride copolymer film or hollow fiber has a thickness of 2 micrometer to 15 micrometers. 
     
     
         19 . A process for separating an olefin from a gas mixture having the olefin's corresponding paraffin, the process comprising
 (i) providing a carbonized polyvinylidene chloride copolymer membrane having a thickness of 1 micrometer to 20 micrometers and an average pore size greater than the olefin or paraffin as determined by gas permeation employing gas probe molecules of differing sizes; and   (ii) flowing the gas mixture through said carbonized polyvinylidene chloride copolymer membrane to produce a permeate first stream having an increased concentration of the olefin and a second retentate stream having an increased concentration of its corresponding paraffin.   
     
     
         20 . The process of  claim 19 , wherein the olefin is ethylene or propylene. 
     
     
         21 . The process of  claim 20 , wherein the paraffin is ethane or propane. 
     
     
         22 . The process of  claim 19 , wherein the average pore size is greater than 4 angstroms. 
     
     
         23 . The process of  claim 22 , wherein the average pore size is greater than 5 angstroms. 
     
     
         24 . The process of  claim 19 , wherein the polyvinylidene chloride copolymer membrane has a thickness of 2 micrometer to 15 micrometers.