Nickel-based superalloy for diffusion bonding and method for diffusion bonding using the same

Abstract

The present invention relates to a nickel-based superalloy for diffusion bonding, which includes a surface depletion layer in a state in which an aluminum (Al) or titanium (Ti) content is depleted, the surface depletion layer being formed to a depth of 50 μm or less from a surface for diffusion bonding, and a method for diffusion bonding using the same.

What is claimed is: 
     
         1 . A nickel-based superalloy for diffusion bonding, comprising:
 a surface depletion layer in which an aluminum (Al) or titanium (Ti) content is depleted,   wherein the surface depletion layer is formed to a depth of 50 μm or less from a surface for diffusion bonding.   
     
     
         2 . The nickel-based superalloy of  claim 1 , wherein the nickel-based superalloy comprises 20.0 to 24.0 wt % of chromium (Cr); 10.0 to 15.0 wt % of cobalt (Co); 8.0 to 10.0 wt % of molybdenum (Mo); 0.8 to 1.5 wt % of aluminum (Al); 0.6 wt % or less of titanium (Ti); and the remainder of nickel (Ni). 
     
     
         3 . The nickel-based superalloy of  claim 1 , wherein when the surface depletion layer is divided into an upper surface depletion layer and a lower surface depletion layer based on the halfway point of the depth of the surface depletion layer, and the upper surface depletion layer has a higher degree of depletion of Al or Ti content compared to the lower surface depletion layer. 
     
     
         4 . A method for diffusion bonding of a nickel-based superalloy, comprising:
 (a) forming an outer oxide film and an inner oxide by pre-oxidizing a nickel-based superalloy parent material;   (b) removing the formed outer oxide film and an inner oxide-containing layer; and   (c) preparing a diffusion-bonded nickel-based superalloy material by performing diffusion bonding on the nickel-based superalloy from which the outer oxide film and inner oxide-containing layer are removed,   wherein, in Step (c), the nickel-based superalloy comprises a surface depletion layer in a state in which an Al or Ti content is depleted, and the surface depletion layer is formed to a depth of 50 μm or less from a surface for diffusion bonding.   
     
     
         5 . The method of  claim 4 , wherein the pre-oxidation in Step (a) is performed under atmospheric conditions at 600 to 1,200° C. for 0.1 to 500 hours. 
     
     
         6 . The method of  claim 4 , wherein, in Step (a), the outer oxide film comprises chromium oxide and has a thickness of 0.1 to 50 μm. 
     
     
         7 . The method of  claim 4 , wherein, in Step (a), the inner oxide comprises aluminum oxide, titanium oxide or a combination thereof, and has a depth of 1 to 100 μm. 
     
     
         8 . The method of  claim 4 , wherein, in Step (c), during the diffusion bonding, the secondary phase formation by Al or Ti at the interface between the nickel-based superalloys is inhibited or reduced. 
     
     
         9 . The method of  claim 4 , further comprising:
 (d) thermally treating the formed diffusion-bonded nickel-based superalloy material at 1,000 to 1,200° C. for 1 to 100 hours.