Sulfonate group-containing polymer and method of producing the same

Abstract

A sulfonate group-containing copolymer is provided which comprising a structural unit (a) derived from a sulfonate group-containing monomer (A); a structural unit (b) derived from a (poly)oxyalkylene monomer (B); a structural unit (c) derived from a carboxyl group-containing monomer (C). The sulfonate group-containing copolymer comprises from 20% to 90% by mass in an acid form equivalent of the structural unit (c) in 100% by mass of all the structural units constituting the sulfonate group-containing copolymer. The product (P×Mw×n) of the ratio by mass P of the structural unit (b) to the structural unit (a) multiplied by the weight average molecular weight Mw of the sulfonate group-containing copolymer multiplied by the value n is from 950,000 to 800,000,000.

1 .- 5 . (canceled) 
     
     
         6 . A sulfonate group-containing copolymer, comprising:
 a structural unit (a) derived from a sulfonate group-containing monomer (A);   a structural unit (b) derived from a (poly)oxyalkylene monomer (B) represented by the following formula (1):   
       
         
           
           
               
               
           
         
       
       wherein R 1  represents a hydrogen atom or a methyl group; R 2  represents a direct bond, CH 2 , or CH 2 CH 2 ; and X 0  represents a structural unit represented by the following formula (2):
   —Zn—OR 0   (2)
 
 
       wherein Z may be the same or different and each represents a structural unit derived from a C 2 -C 5  alkylene oxide; R 0  represents hydrogen atom or a methyl group; and n is an integer of from 5 to 100; and
 a structural unit (c) derived from a carboxyl group-containing monomer (C) that is at least one selected from the group consisting of (meth)acrylic acid, maleic acid, maleic anhydride, and salts thereof, 
 wherein the sulfonate group-containing copolymer comprises from 2% to 38% by mass of the structural unit (a), from 8% to 70% by mass of the structural unit (b), and from 20% to 90% by mass in an acid form equivalent of the structural unit (c) in 100% by mass of all the structural units constituting the sulfonate group-containing copolymer, 
 wherein the product (P×Mw×n) of the ratio by mass P of the structural unit (b) to the structural unit (a) multiplied by the weight average molecular weight Mw of the sulfonate group-containing copolymer multiplied by the value n in the formula (2) is from 950,000 to 33,300,000, 
 wherein the sulfonate group-containing monomer (A) is at least one of 2-acrylamide-2-methylpropanesulfonic acid and a compound represented by the following formula (3): 
 
       
         
           
           
               
               
           
         
       
       wherein R 3  represents a hydrogen atom or a methyl group; R 4  represents a direct bond, CH 2 , or CH 2 CH 2 ; X and Y each represent a hydroxy group or SO 3 M where M represents a hydrogen atom, Li, Na, or K, and at least one of X and Y is SO 3 M,
 wherein the sulfonate group-containing copolymer optionally comprises a structural unit (e) derived from a monomer (E) that is none of the monomer (A), the monomer (B), and the monomer (C) in an amount no more than 20% by mass based on 100% by mass of the structural units (a), (b), (c), and (e), 
 wherein the degree of neutralization of the sulfonate group-containing copolymer is 1 to 100 mol %, and. 
 
       wherein an anti-redeposition property exhibited by the sulfonate group-containing copolymer, evaluated as follows, is at least 64.8%:
 <Evaluation of Anti-Redeposition Properties> 
 In evaluation of anti-redeposition properties under high hardness condition, clay is used in item (4) as soil 
 (1) A cotton cloth obtained from Testfabrics, Inc. is cut into 5 cm×5 cm to prepare white cloths and whiteness of each of the white clothes is previously measured as reflectance using colorimetry color difference meter SE6000 type produced by Nippon Denshoku Industries Co., Ltd. 
 (2) Pure water is added to calcium chloride dihydrate (5.0 g) to prepare hard water (17 kg) 
 (3) Pure water is added to polyoxyethylene (8) lauryl ether (4.0 g) to prepare an aqueous surfactant solution (100.0 g) and pH is controlled to 8.5 with sodium hydroxide. 
 (4) The temperature of a Terg-o-Tometer is set at 25° C., to a pot are added hard water (1 L), an aqueous surfactant solution (5 g), a 2% (solids content) aqueous polymer solution (1 g), and test powder 1 (class 11) (1 g) according to JIS Z 8901, the contents are stirred for 1 min at 100 rpm, five white cloths are put into the solution, and the solution is stirred for 10 min at 100 rpm 
 (5) The white cloths are wrung by hand, and hard water (1 L) at 25° C. is charged into the pot, and is stirred for 2 min at 100 rpm 
 (6) Each of the white cloths is pressed with a filler cloth to be dried while smoothing wrinkles, and the dried clothes are measured for whiteness again as reflectance with the above colorimetric difference meter 
 (7) From the measurement results, the anti-redeposition performance is determined according to formula
   Anti-redeposition performance (%)=(whiteness after washing)/(whiteness of original white cloth)×100
 
 
 
     
     
         7 . The sulfonate group-containing copolymer according to  claim 6 ,
 wherein the sulfonate group-containing copolymer has a weight average molecular weight Mw of from 20,000 to 200,000.   
     
     
         8 . The sulfonate group-containing copolymer according to  claim 6 ,
 wherein the sulfonate group-containing copolymer has a ratio by mass P of the structural unit (b) to the structural unit (a) of from 1.2 to 20.   
     
     
         9 . The sulfonate group-containing copolymer according to  claim 6 , wherein the sulfonate group-containing copolymer comprises from 2% to 30% by mass of the structural unit (a). 
     
     
         10 . The sulfonate group-containing copolymer according to  claim 6 , wherein the sulfonate group-containing copolymer comprises 8% to 50% by mass of the structural unit (b).