Aluminum alloy for vehicle outer panels and method for producing the same

Abstract

Disclosed herein are an aluminum alloy for vehicle outer panels and a method for producing the aluminum alloy thereby improving elasticity, formability, and dent resistance by maximizing a generation of boride compound to improve stiffness and NVH characteristics. The aluminum alloy for vehicle outer panels includes Ti, B, Mg, and a balance of the aluminum alloy being Al and includes both of an AlB 2 phase and a TiB 2 phase as a reinforcing phase. In particular, a composition ratio of Ti:B:Mg is of about 1:about 2.0-2.5:about 5.0-6.0 and B is included in an amount of about 1.1 to 2.5 wt % based on the total weight of the alloy composition.

1 - 3 . (canceled) 
     
     
         4 . A method for producing an aluminum alloy for vehicle outer panels, comprising:
 charging, in a melting vessel, at least one from an aluminum-titanium (Al—Ti) master alloy, an aluminum-boron (Al—B) master alloy, and an aluminum (Al) salt compound in an aluminum (Al) molten metal containing Mg in an amount of 0.5 to 5 wt % to form a molten metal, a composition ratio of Ti:B:Mg is of about 1:about 2.0-2.5:about 5.0-6.0; and   agitating the molten metal by using an agitator to disperse an AlB 2  phase and a TiB 2  phase that are generated as a reinforcing phase by a spontaneous reaction.   
     
     
         5 . The method of  claim 4 , wherein the agitator is formed to have a length of about 0.4 times or greater of a diameter of the melting vessel, and
 in the agitating, the molten metal is agitated at a speed of about 500 rpm or greater.   
     
     
         6 . The method of  claim 4 , wherein the Al—Ti master alloy includes Ti in an amount of about 5 to 20 wt % based on the total weight of the Al—Ti master alloy and a balance of the Al—Ti master alloy being Al. 
     
     
         7 . The method of  claim 4 , wherein the Al—B master alloy includes B in an amount of about 3 to 10 wt % based on the total weight of the Al—B master alloy and a balance of the Al—B master alloy being Al. 
     
     
         8 . The method of  claim 4 , the Al salt compound includes aluminum salts in an amount of about 75 wt % based on the total weight of the Al salt compound. 
     
     
         9 . (canceled)