Flexible Superhydrophobic and/or Oleophobic Polyurethane Coatings

Abstract

This disclosure deals with novel formulations to create highly durable flexible hydrophobic, superhydrophobic, oleophobic and/or superoleophobic surfaces. The formulations of this invention can be applied by dip, spray and painting processes.

1 .- 38 . (canceled) 
     
     
         39 . A system for forming a hydrophobic coating comprising a first polyurethane forming composition and a second composition:
 wherein the first polyurethane forming composition, which is uncured, comprises
 i) one or more polyisocyanates and one or more polyester polyalcohols that react to form a polyurethane, wherein said one or more polyalcohols each have a molecular weight from about 150 to about 10,000 Daltons and an average molar hydroxyl functionality from about 2.0 to about 2.5, 
 ii) about 2% to about 20% by weight of one or more independently selected first particles having a size of about 30 μm to about 225 μm, and 
 iii) one or more independently selected solvents; and 
   wherein the second composition, which is uncured, comprises
 i) one or more independently selected second particles having a size of about 1 nm to about 25 μm, wherein said second particles comprise one or more independently selected hydrophobic and/or oleophobic moieties bound, either directly or indirectly, to said second particles, and 
 ii) one or more independently selected solvents, wherein said second particles are present in a weight percent range selected from 0.1-5.0, based on the weight of the one or more solvents and second particles; 
   wherein the polyisocyanates and the polyester polyalcohols are provided as two or more components that are mixed to form the first polyurethane forming composition, and   wherein the two or more components that are mixed to form the first polyurethane forming composition are provided separated from the second composition.   
     
     
         40 . A system for forming a hydrophobic coating comprising a first polyurethane forming composition and a second composition:
 wherein the first polyurethane forming composition, which is uncured, comprises
 i) one or more polyisocyanates and one or more polyester polyalcohols that react to form a polyurethane, wherein said one or more polyalcohols have a molecular weight from about 150 to about 10,000 Daltons and an average molar hydroxyl functionality from about 2.0 to about 2.5, 
 ii) about 2% to about 20% by weight of one or more independently selected first particles having a size of about 30 μm to about 225 μm, and 
 iii) optionally comprises one or more independently selected solvents; and 
   wherein the second composition, which is uncured, comprises per 100 parts by weight
 i) 0.1 to 3.5 parts by weight of one or more independently selected second particles having a size of about 1 nm to about 25 μm, wherein said second particles comprise one or more independently selected hydrophobic or oleophobic moieties bound, either directly or indirectly, to said second particles, or one or more siloxanes or silazanes associated with said second particles, 
 ii) 0.1 to 1.0 parts by weight of a fluorinated polyolefin; 
 and/or 
 0.06 to 0.6 parts by weight of a fluoroethylene-alkyl vinyl ether (FEVE) copolymer, having an average molecular weight of about 1,000 to about 3,000 Daltons, and 
 iii) one or more independently selected solvents for the remainder of a total of 100 parts by weight; 
   wherein the polyisocyanates and the polyester polyalcohols are provided as two or more components that are mixed to form the first polyurethane forming composition, and   wherein the two or more components that are mixed to form the first polyurethane forming composition are provided separated from the second composition.   
     
     
         41 . The system of  claim 40 , wherein said one or more polyester polyalcohols comprise one or more hydroxyl bearing polyether, polyamide, and/or polyacrylate polymers. 
     
     
         42 . The system of  claim 40 , comprising a single type of polyester polyalcohol that comprises 0, 1, 2, or 3 terminal hydroxyl groups per molecule, or a mixture of two or more polyester polyalcohols that comprise 0-1, 1-2, or 2-3 terminal hydroxyl functionalities. 
     
     
         43 . The system of  claim 41 , wherein said one or more polyester polyalcohols comprise monomers with a molecular weight in a range selected from 60-150 g/mole. 
     
     
         44 . The system of  claim 40 , wherein the second composition comprises a FEVE. 
     
     
         45 . The system of  claim 40 , wherein the one or more polyester polyalcohols have no terminal hydroxyl groups. 
     
     
         46 . A method of forming a hydrophobic coating on all or a portion of the surface of an object comprising the steps:
 (a) optionally applying or treating the surface with a primer to form a primed surface,   (b) forming a base coat by applying an uncured first polyurethane forming composition comprising
 i) one or more polyisocyanates and one or more polyester polyalcohols that react to form a polyurethane, wherein said one or more polyalcohols have a molecular weight from about 150 to about 10,000 Daltons and an average molar hydroxyl functionality from about 2.0 to about 2.5, 
 ii) about 2% to about 20% by weight of one or more independently selected first particles having a size of about 30 μm to about 225 μm, and 
 iii) optionally comprises one or more independently selected solvents 
 to at least a portion of said surface, or to at least a portion of said primed surface; and 
   (c) applying an uncured second composition comprising
 i) 0.1 to 3.5 parts by weight of one or more independently selected second particles having a size of about 1 nm to about 25 μm, wherein said second particles comprise one or more independently selected hydrophobic or oleophobic moieties bound, either directly or indirectly, to said second particles, or one or more siloxanes or silazanes associated with said second particles, 
 ii) 0.1 to 1.0 parts by weight of a fluorinated polyolefin; 
 and/or 
 0.06 to 0.6 parts by weight of a fluoroethylene-alkyl vinyl ether (FEVE) copolymer, having an average molecular weight of about 1,000 to about 3,000 Daltons, and 
 iii) one or more independently selected solvents for the remainder of a total of 100 parts by weight 
 to all or a portion of the base coat to form said coating, 
   wherein said coating has either hydrophobic or superhydrophobic properties, and optionally is also oleophobic or superoleophobic,   wherein the polyisocyanates and the polyester polyalcohols are provided as two or more components that are mixed to form the first polyurethane forming composition, and   wherein the two or more components that are mixed to form the first polyurethane forming composition are provided separated from the second composition.   
     
     
         47 . The method of  claim 46 , wherein said steps of applying said first polyurethane forming composition and applying said second composition are conducted by methods selected independently from painting, printing, stamping, rolling, dipping, spin coating, spraying, and electrostatic spraying. 
     
     
         48 . A coating prepared by the method according to  claim 46 . 
     
     
         49 . The coating of  claim 48 , wherein said coating is superhydrophobic and/or superoleophobic. 
     
     
         50 . The coating according to  claim 49 , wherein said coating has an ultimate strength greater than about 20 mega Pascals (MPa) according to ASTM D412 and/or an ultimate elongation of greater than 90%, measured according to ASTM D412. 
     
     
         51 . The coating according to  claim 48 , wherein said coating has a modulus at 100% elongation of greater than 10, 11, 12, or 13 mega Pascals (MPa) according to ASTM D412. 
     
     
         52 . The coating according to  claim 48 , having an elongation at break of greater than about 100%. 
     
     
         53 . The coating according to  claim 48 , wherein said coating is superhydrophobic and retains its superhydrophobicity after being subjected to greater than 30 cycles on a Taber Abraser using CS-0 or CS-10 wheels and a 250 gram load at 95 rpm at room temperature, wherein the end of superhydrophobicity is determined to be the point when more than half of the water droplets applied to the portion of the surface subject to the action of the wheels do not roll off the surface when the surface is inclined at a 5 degree angle at room temperature. 
     
     
         54 . The coating according to  claim 53 , wherein said coating retains its superhydrophobicity after being subjected to greater than 20 cycles on a Taber Abraser using CS-0 or CS-10 wheels and a 1,000 gram load at 95 rpm at 20° C.-25° C., wherein the end of superhydrophobicity is determined to be the point when more than half of the water droplets applied to the portion of the surface subject to the action of the wheels do not roll off the surface when the surface is inclined at a 5 degree angle at room temperature. 
     
     
         55 . The coating according to  claim 48 , wherein said coating is superhydrophobic and when said coating is applied to a substantially planar surface about 10 cm×about 10 cm, it continues to display superhydrophobic behavior after being subjected to a continuous shower of about six liters of water per minute delivered within a 60 cm diameter circular area from a showerhead placed about 1.5 meters above the substantially planar surface at about 20° C. to 25° C. for greater than 0.5 hours. 
     
     
         56 . The coating of  claim 55 , wherein, when said coating is subjected to said continuous shower test for a period of time sufficient to lose superhydrophobic behavior, the coating regains superhydrophobic behavior following drying at 20° C. to 25° C. and one atmosphere of pressure, said shower testing and drying collectively comprising a single test cycle, and wherein said coating regains superhydrophobic behavior following more than 200 test cycles. 
     
     
         57 . A system for forming a coating comprising:
 a first polyurethane forming composition, which is uncured, and a second composition, which is uncured;
 wherein the first polyurethane forming composition
 i) comprises one or more polyisocyanates and one or more polyamides, and/or polyacrylate polyalcohol polymers that react to form a polyurethane, wherein said one or more polyalcohol polymers have a molecular weight from about 150 to about 10,000 Daltons and an average molar hydroxyl functionality from about 2.0 to about 2.5, 
 ii) optionally comprises one or more independently selected first particles having a size of about 30 μm to about 225 μm, wherein, when said first particles are present, the first polyurethane forming composition comprises from about 5% to about 20% of said first particles by weight, and 
 iii) optionally comprises one or more independently selected solvents; and 
 
 wherein the second composition comprises per 100 parts by weight
 i) 0.1 to 3.5 parts by weight of one or more independently selected second particles having a size of about 1 nm to about 25 μm, wherein said second particles comprise one or more independently selected hydrophobic or oleophobic moieties bound, either directly or indirectly, to said second particles, or one or more siloxanes or silazanes associated with said second particles, 
 ii) 0.1 to 1.0 parts by weight of a fluorinated polyolefin; 
 and/or 
 0.06 to 0.6 parts by weight of a fluoroethylene-alkyl vinyl ether (FEVE) copolymer, having an average molecular weight of about 1,000 to about 3,000 Daltons, and 
 iii) one or more independently selected solvents for the remainder of a total of 100 parts by weight, 
 
 wherein the polyisocyanates and the polyester polyalcohols are provided as two or more components that are mixed to form the first polyurethane forming composition, and 
 wherein the two or more components that are mixed to form the first polyurethane forming composition are provided separated from the second composition. 
   
     
     
         58 . The system of  claim 57 , wherein the second composition comprises a FEVE. 
     
     
         59 . A polyurethane forming composition comprising:
 i) one or more polyisocyanates and one or more polyester polyalcohols that react to form a polyurethane, wherein the one or more polyalcohols have a molecular weight from about 150 to about 10,000 Daltons and an average molar hydroxyl functionality from about 2.0 to about 2.5; and   ii) about 2% to about 20% by weight of one or more independently selected particles having a size of about 30 μm to about 225 μm; and   wherein the polyurethane forming composition optionally comprises one or more independently selected solvents.   
     
     
         60 . The polyurethane forming composition of  claim 59 , wherein the polyurethane forming composition is provided as two or more components that are mixed to form the polyurethane forming composition. 
     
     
         61 . A composition comprising per 100 parts by weight of:
 i) 0.1 to 3.5 parts by weight of one or more independently selected particles having a size of about 1 nm to about 25 μm, wherein the particles comprise one or more independently selected hydrophobic or oleophobic moieties bound, either directly or indirectly, to the particles, or one or more siloxanes or silazanes associated with the particles;   ii) 0.1 to 1.0 parts by weight of a fluorinated polyolefin,   and/or   0.06 to 0.6 parts by weight of a fluoroethylene-alkyl vinyl ether (FEVE) copolymer, having an average molecular weight of about 1,000 to about 3,000 Daltons; and   iii) one or more independently selected solvents for the remainder of a total of 100 parts by weight.