Multiple layer interlayer resisting defect formation

Abstract

Multilayered interlayers comprising stiff skin or outer layers and a soft core layer(s) are disclosed. The multilayered interlayers comprise: a first polymer layer (skin layer) comprising plasticized poly(vinyl butyral) resin; a second polymer layer (core layer) comprising a blend of two (or more) plasticized poly(vinyl butyral) resins having different residual hydroxyl content; and optionally a third polymer layer (skin layer) comprising plasticized poly(vinyl butyral) resin.

1 . A polymer interlayer that resists formation of iceflower defect, the polymer interlayer comprising:
 at least one soft layer wherein the soft layer comprises a blend of two or more poly(vinyl butyral) resins comprising:   a first poly(vinyl butyral) resin having a first residual hydroxyl content;   a second poly(vinyl butyral) resin having a second residual hydroxyl content, wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent;   a plasticizer, wherein the first poly(vinyl butyral) resin, the second poly(vinyl butyral) resin, and the plasticizer are mixed and melt-extruded to form the at least one soft layer;   at least one stiffer layer comprising a third poly(vinyl butyral) resin having a third residual hydroxyl content and a plasticizer, wherein the difference between the third residual hydroxyl content and at least one of the first and second residual hydroxyl contents is at least 2.0 weight percent;   wherein the polymer interlayer has a damping loss factor (n) (as measured by Mechanical Impedance Measurement according to ISO 16940) of at least about 0.15.   
     
     
         2 . The polymer interlayer of  claim 1 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 5 weight percent to about 45 weight percent. 
     
     
         3 . The polymer interlayer of  claim 1 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 10 weight percent to about 40 weight percent. 
     
     
         4 . The polymer interlayer of  claim 1 , wherein the soft layer of the polymer interlayer has at least one glass transition temperature (T g ) less than 15° C. 
     
     
         5 . The polymer interlayer of  claim 1 , wherein the residual hydroxyl content of the third poly(vinyl butyral) resin is the same as the residual hydroxyl content of the first poly(vinyl butyral) resin or the second poly(vinyl butyral) resin. 
     
     
         6 . The polymer interlayer of  claim 1 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 4.0 weight percent. 
     
     
         7 . The polymer interlayer of  claim 1 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 6.0 weight percent. 
     
     
         8 . The polymer interlayer of  claim 1 , wherein the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between the at least two different glass transition temperatures (T g ) is at least 3° C. 
     
     
         9 . A polymer interlayer that resists formation of iceflower defect, the polymer interlayer comprising:
 at least one soft layer wherein the soft layer comprises a blend of two or more poly(vinyl butyral) resins comprising:   a first poly(vinyl butyral) resin having a first residual hydroxyl content of from 7 to 14 weight percent;   a second poly(vinyl butyral) resin having a second residual hydroxyl content of from 12 to 35 weight percent;   wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent;   a plasticizer, wherein the first poly(vinyl butyral) resin, the second poly(vinyl butyral) resin, and the plasticizer are mixed and melt-extruded to form the at least one soft layer;   at least one stiffer layer comprising a third poly(vinyl butyral) resin having a third residual hydroxyl content of from 15 to 35 weight percent and a plasticizer,   wherein the polymer interlayer has a damping loss factor (η) (as measured by Mechanical Impedance Measurement according to ISO 16940) of at least about 0.15.   
     
     
         10 . The polymer interlayer of  claim 9 , wherein the soft layer of the polymer interlayer has at least one glass transition temperature (T g ) less than 15° C. 
     
     
         11 . The polymer interlayer of  claim 9 , wherein the residual hydroxyl content of the third poly(vinyl butyral resin) is the same as the residual hydroxyl content of the first poly(vinyl butyral resin) or the second poly(vinyl butyral resin). 
     
     
         12 . The polymer interlayer of  claim 9 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 4.0 weight percent. 
     
     
         13 . The polymer interlayer of  claim 9 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 6.0 weight percent. 
     
     
         14 . The polymer interlayer of  claim 9 , wherein the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between at least two different glass transition temperatures (T g ) is at least 3° C. 
     
     
         15 . A polymer interlayer that resists formation of iceflower defects, the polymer interlayer comprising:
 at least one soft layer wherein the soft layer comprises a blend of two or more poly(vinyl butyral) resins comprising:   a first poly(vinyl butyral) resin having a first residual hydroxyl content;   a second poly(vinyl butyral) resin having a second residual hydroxyl content,   wherein the first poly(vinyl butyral) resin has a first glass transition temperature (T g ) of the plasticized first resins, and the second poly(vinyl butyral) resin has a second glass transition temperature (T g ) of the plasticized second resin,   wherein at least one of the first and second glass transition temperature is less than 15° C.,   and wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 2.0 weight percent;   at least one stiffer layer comprising a third poly(vinyl butyral) resin having a third residual hydroxyl content and a plasticizer, wherein the difference between the third residual hydroxyl content and at least one of the first and second residual hydroxyl contents is at least 2.0 weight percent;   wherein the polymer interlayer has a damping loss factor (η) (as measured by Mechanical Impedance Measurement according to ISO 16940) of at least about 0.15.   
     
     
         16 . The polymer interlayer of  claim 15 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 5 weight percent to about 45 weight percent. 
     
     
         17 . The polymer interlayer of  claim 15 , wherein the second poly(vinyl butyral) resin is present in an amount of from about 10 weight percent to about 40 weight percent. 
     
     
         18 . The polymer interlayer of  claim 15 , wherein the polymer interlayer has at least two different glass transition temperatures (T g ) and the difference between at least two different glass transition temperatures (T g ) is at least 3° C. 
     
     
         19 . The polymer interlayer of  claim 15 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 4.0 weight percent. 
     
     
         20 . The polymer interlayer of  claim 15 , wherein the difference between the first residual hydroxyl content and the second residual hydroxyl content is at least 6.0 weight percent.