Coated manganese doped phosphors

Abstract

A process for preparing a population of coated phosphor particles is presented. The process includes combining particles of a phosphor of formula I: A x [MF y ]:Mn 4+ with a first solution including a compound of formula II: A x [MF y ] to form a suspension, where A is Li, Na, K, Rb, Cs, or a combination thereof; M is Si, Ge, Sn, Ti, Zr, Al, Ga, In, Sc, Hf, Y, La, Nb, Ta, Bi, Gd, or a combination thereof; x is an absolute value of a charge of the [MF y ] ion; and y is 5, 6 or 7. The process further includes combining a second solution including a source A + ions with the suspension.

1 . A process for preparing a population of coated phosphor particles comprising:
 combining particles of a phosphor of formula I with a first solution comprising a compound of formula II to form a suspension; and   combining a second solution comprising a source of A +  ions with the suspension,
   A x [MF y ]:Mn 4+    (I)
 
   A x [MF y ]   (II)
 
   
       wherein
 A is Li, Na, K, Rb, Cs, or a combination thereof; 
 M is Si, Ge, Sn, Ti, Zr, Al, Ga, In, Sc, Hf, Y, La, Nb, Ta, Bi, Gd, or a combination thereof; 
 x is an absolute value of a charge of an [MF y ] ion; and 
 y is 5, 6, or 7. 
 
     
     
         2 . The process according to  claim 1 , wherein
 A is Na, K, or a combination thereof; and   M is Si, Ge, Ti, Zr, or a combination thereof.   
     
     
         3 . The process according to  claim 1 , wherein the source of A +  ions comprises a compound selected from a halide, sulphate, phosphate, acetate, and combinations thereof. 
     
     
         4 . The process according to  claim 3 , wherein the source of A +  ions comprises KF, KHF 2 , KCl, KBr, KI, K 2 SO 4 , K 3 PO 4 , CH 3 COOK, or a combination thereof. 
     
     
         5 . The process according to  claim 1 , wherein the first solution, the second solution or both the first solution and the second solution comprises hydrofluoric acid. 
     
     
         6 . The process according to  claim 1 , wherein the second solution is added to the suspension at a rate less than 100 milliliters/minute. 
     
     
         7 . The process according to  claim 1 , wherein the second solution is added to the suspension at a rate in a range from about 0.1 millimeter/minute to about 10 milliliters/minute. 
     
     
         8 . The process according to  claim 1 , wherein a molar ratio of the source of A +  ions to the compound of formula II is in a range from about 1:1 to about 1:20. 
     
     
         9 . The process according to  claim 1 , wherein the phosphor of formula I is K 2 SiF 6 :Mn 4+ . 
     
     
         10 . The process according to  claim 1 , wherein the compound of formula II is K 2 SiF 6 . 
     
     
         11 . A process for preparing a population of coated phosphor particles comprising:
 combining particles of K 2 SiF 6 :Mn 4+  with a first solution comprising K 2 SiF 6  to form a suspension; and   combining a second solution comprising KF with the suspension.