Impact Strength Modifier for Chlorine-Containing Resin, Chlorine-Containing Resin Composition and Molded Body of Chlorine-Containing Resin Composition

Abstract

Disclosed is an impact strength modifier (α) for a chlorine-containing resin, comprising a powder of a graft copolymer (A) obtained by graft polymerizing one or more kinds of vinyl monomers (b1) onto a polyorganosiloxane rubber (A1) or a composite rubber (A2) containing a polyorganosiloxane rubber and a polyalkyl (meth)acrylate rubber, wherein the specific surface area of the powder of the graft copolymer (A) measured by a nitrogen gas adsorption method is from 0.6 to 30 m 2 /g, and the pH of water used for extraction under conditions, in which (1) in an oven at 180° C., 5.0 g of the powder of the graft copolymer (A) is left to stand still and heated for 15 minutes, and (2) after the heating, the powder is dispersed in 100 ml of heated pure water and extracted for 1 hour at 70° C. while stirring, is from 4 to 11.

1 . An impact strength modifier (α) for a chlorine-containing resin,
 wherein the impact strength modifier comprises a powder of a graft copolymer (A) obtained by graft polymerizing one or more vinyl monomers (b1) onto a polyorganosiloxane rubber (A1) or a composite rubber (A2) containing a polyorganosiloxane rubber and a polyalkyl (meth)acrylate rubber, and 
 wherein
 a specific surface area of the powder of the graft copolymer (A) measured by a nitrogen gas adsorption method is from 0.6 to 30 m 2 /g and 
 water used for extraction under the following conditions (1) and (2) is at a pH of from 4 to 11: 
 (1) in an oven at 180° C., 5.0 g of the powder of the graft copolymer (A) is left to stand still and heated for 15 minutes, and 
 (2) after the heating, the powder is dispersed in 100 ml of water and extracted for 1 hour at 70° C. while stirring. 
 
 
     
     
         2 . The impact strength modifier (α) for a chlorine-containing resin according to  claim 1 , wherein the powder of the graft copolymer (A) is obtained by spray drying latex of the graft copolymer (A). 
     
     
         3 . The impact strength modifier (α) for a chlorine-containing resin according to  claim 1 , wherein a content of an emulsifier having a thermal decomposition temperature measured by a TG/DTA measuring device of less than 200° C. is 0.1 parts by mass or less with respect to 100 parts by mass of the modifier (α). 
     
     
         4 . The impact strength modifier (α) for a chlorine-containing resin according to  claim 1 , wherein the impact strength modifier further comprises at least one kind of emulsifier selected from the group consisting of sodium dodecylbenzenesulfonate, sodium alkyl diphenyl ether disulfonate, sodium dialkylsulfosuccinate and a polyoxyethylene distyrenated phenyl ether. 
     
     
         5 . The impact strength modifier (α) for a chlorine-containing resin according to  claim 1 , wherein an amount of an organosiloxane contained in the powder of the graft copolymer (A) is 0.4% by mass or less. 
     
     
         6 . The impact strength modifier (α) for a chlorine-containing resin according to  claim 1 , wherein the vinyl monomer (b1) is at least one monomer selected from the group consisting of an aromatic alkenyl compound, an ester of (meth)acrylic acid and a vinyl cyanide compound. 
     
     
         7 . (canceled) 
     
     
         8 . A chlorine-containing resin composition, comprising the impact strength modifier (α) for a chlorine-containing resin according to  claim 1  and a chlorine-containing resin (β). 
     
     
         9 . The chlorine-containing resin composition according to  claim 8 , wherein the composition contains the impact strength modifier (α) for a chlorine-containing resin at from 0.1 to 30 parts by mass with respect to 100 parts by mass of the chlorine-containing resin (β). 
     
     
         10 . A molded body obtained by molding the chlorine-containing resin composition according to  claim 8 . 
     
     
         11 . A molded body obtained by molding the chlorine-containing resin composition according to  claim 9 .