Steel sheet for steel belt and process for manufacturing same, and steel belt

Abstract

Manufacturing a steel sheet for a steel belt includes hot rolling a steel slab containing, in mass %, 0.60 to 0.80% of C, 1.0% or less of Si, 0.10 to 1.0% of Mn, 0.020% or less P, 0.010% or less S, 0.1 to 1.0% of Cr, 0 to 0.5% of V, 0 to 0.1% of Ti, 0 to 0.1% of Nb, and 0 to 0.01% of B, the balance Fe and unavoidable impurities, under a finish hot rolling temperature of 800 to 900° C. An average cooling rate from finish rolling to coiling is 20° C. per second or more. A coiling temperature is 450 to 650° C. The hot-rolled slab is cold rolled with a total rolling reduction ratio of 40% or more and a reduction ratio per one pass of less than 12%, without performing a heat treatment. The cold-rolled slab is aged at 200 to 500° C. for 0.5 to 30 hours.

1 . A process for manufacturing a steel sheet for a steel belt, comprising: subjecting a slab of steel having a chemical composition containing from 0.60 to 0.80% of C, 1.0% or less of Si, from 0.10 to 1.0% of Mn, 0.020% or less of P, 0.010% or less of S, from 0.1 to 1.0% of Cr, from 0 to 0.5% of V, from 0 to 0.1% of Ti, from 0 to 0.1% of Nb, and from 0 to 0.01% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities, to hot rolling under a condition of a finish hot rolling temperature of from 800 to 900° C., an average cooling rate from the finish rolling to coiling of 20° C. per second or more, and a coiling temperature of from 450 to 650° C.; then subjecting the hot-rolled slab to cold rolling of a total rolling reduction ratio of 40% or more and a reduction ratio per one pass of less than 12%, without performing a heat treatment; and then subjecting the cold-rolled slab to an aging treatment of maintaining a temperature of from 200 to 500° C. for a period of from 0.5 to 30 hours. 
     
     
         2 . A process for manufacturing a steel sheet for a steel belt, comprising: subjecting a slab of steel having a chemical composition containing from 0.60 to 0.80% of C, 1.0% or less of Si, from 0.10 to 1.0% of Mn, 0.020% or less of P, 0.010% or less of S, from 0.1 to 1.0% of Cr, from 0 to 0.5% of V, from 0 to 0.1% of Ti, from 0 to 0.1% of Nb, and from 0 to 0.01% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities, to hot rolling under a condition of a finish hot rolling temperature of from 800 to 900° C., an average cooling rate from the finish rolling to coiling of 20° C. per second or more, and a coiling temperature of from 450 to 650° C.; then subjecting the hot-rolled slab to cold rolling of a total rolling reduction ratio of 40% or more and a reduction ratio per one pass of less than 12%, without performing a heat treatment; and then subjecting the cold-rolled slab to an aging treatment of maintaining a temperature of from 200 to 500° C. for a period of from 0.5 to 30 hours, thereby producing a steel sheet having a volume fraction of a pearlite structure in a metallic structure of 70% or more, a tensile strength in the rolling direction of 1,100 MPa or more, and a crack propagation resistance according to the following item (A) of 600 MPa or more:
 (A) a test piece shown in  FIG. 1  is subjected to a tensile test in the longitudinal direction thereof (which agrees with the rolling direction) at room temperature and a tension speed of 0.3 mm/min, so as to provide a load-elongation curve, from which a maximum load is obtained, and a value obtained by dividing the maximum load by an initial cross sectional area (45 mm×thickness) is designated as the crack propagation resistance (unit: MPa). 
 
     
     
         3 . A process for manufacturing a steel sheet for a steel belt, comprising: subjecting a slab of steel having a chemical composition containing more than 0.60% and 0.80% or less of C, from 0.10 to 1.00% of Si, from 0.10 to 1.00% of Mn, from 0.002 to 0.020% of P, from 0.001 to 0.010% of S, from 0.10 to 1.00% of Cr, from 0 to 0.50% of V, from 0 to 0.10% of Ti, from 0 to 0.10% of Nb, and from 0 to 0.010% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities, to hot rolling under a condition of a finish hot rolling temperature of from 800 to 900° C., an average cooling rate from the finish rolling to coiling of 25° C. per second or more, and a coiling temperature of from 450 to 650° C.; then subjecting the hot-rolled slab to cold rolling of a total rolling reduction ratio of 40% or more and a reduction ratio per one pass of less than 12%, without performing a heat treatment; and then subjecting the cold-rolled slab to an aging treatment of maintaining a temperature of from 200 to 500° C. for a period of from 0.5 to 30 hours. 
     
     
         4 . A process for manufacturing a steel sheet for a steel belt, comprising: subjecting a slab of steel having a chemical composition containing more than 0.60% and 0.80% or less of C, from 0.10 to 1.00% of Si, from 0.10 to 1.00% of Mn, from 0.002 to 0.020% of P, from 0.001 to 0.010% of S, from 0.10 to 1.00% of Cr, from 0 to 0.50% of V, from 0 to 0.10% of Ti, from 0 to 0.10% of Nb, and from 0 to 0.010% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities, to hot rolling under a condition of a finish hot rolling temperature of from 800 to 900° C., an average cooling rate from the finish rolling to coiling of 25° C. per second or more, and a coiling temperature of from 450 to 650° C.; then subjecting the hot-rolled slab to cold rolling of a total rolling reduction ratio of 40% or more and a reduction ratio per one pass of less than 12%, without performing a heat treatment; and then subjecting the cold-rolled slab to an aging treatment of maintaining a temperature of from 200 to 500° C. for a period of from 0.5 to 30 hours, thereby producing a steel sheet having a volume fraction of a pearlite structure in a metallic structure of 90% or more, a tensile strength in the rolling direction of 1,300 MPa or more, and a crack propagation resistance according to the following item (A) of 600 MPa or more:
 (A) a test piece shown in  FIG. 1  is subjected to a tensile test in the longitudinal direction thereof (which agrees with the rolling direction) at room temperature and a tension speed of 0.3 mm/min, so as to provide a load-elongation curve, from which a maximum load is obtained, and a value obtained by dividing the maximum load by an initial cross sectional area (45 mm×thickness) is designated as the crack propagation resistance (unit: MPa). 
 
     
     
         5 . The process for manufacturing a steel sheet for a steel belt according to  claim 1 , wherein in the cold rolling, the reduction ratio per one pass is more preferably 10% or less, and the total rolling reduction ratio is 40% or more. 
     
     
         6 . The process for manufacturing a steel sheet for a steel belt according to  claim 1 , wherein in the every pass of the cold rolling, the material temperature is maintained at 110° C. or less. 
     
     
         7 . The process for manufacturing a steel sheet for a steel belt according to  claim 1 , wherein the process further comprises performing temper rolling of a rolling reduction ratio of 10% or less after the aging treatment. 
     
     
         8 . A steel sheet for a steel belt, having a chemical composition containing more than 0.60% and 0.80% or less of C, from 0.10 to 1.00% of Si, from 0.10 to 1.00% of Mn, from 0.002 to 0.020% of P, from 0.001 to 0.010% of S, from 0.10 to 1.00% of Cr, from 0 to 0.50% of V, from 0 to 0.10% of Ti, from 0 to 0.10% of Nb, and from 0 to 0.010% of B, all in terms of percentage by mass, with the balance of Fe and unavoidable impurities; having a metallic structure having a volume fraction of a pearlite structure of 90% or more, and the balance of a pro-eutectoid ferrite phase; and having a tensile strength in the rolling direction of 1,300 MPa or more, and a crack propagation resistance according to the following item (A) of 600 MPa or more:
 (A) a test piece shown in  FIG. 1  is subjected to a tensile test in the longitudinal direction thereof (which agrees with the rolling direction) at room temperature and a tension speed of 0.3 mm/min, so as to provide a load-elongation curve, from which a maximum load is obtained, and a value obtained by dividing the maximum load by an initial cross sectional area (45 mm×thickness) is designated as the crack propagation resistance (unit: MPa).   
     
     
         9 . A steel belt comprising the steel sheet according to  claim 8  formed into an endless belt by welding.