Method for three-dimensionally bending workpiece and bent product

Abstract

A method for three-dimensionally bending a workpiece comprises feeding the workpiece by a feeding unit provided at an upstream side of the workpiece, supporting the workpiece by a supporting unit at a downstream side of the feeding unit, processing the workpiece by clamping the workpiece with a three-dimensionally movable unit that is provided downstream of the supporting unit, heating a local part of the workpiece in a temperature range which allows quenching to be performed, applying a bending moment to the heated local part of the workpiece by the three-dimensionally movable unit in association with the supporting position and/or the moving speed of the workpiece after the heating step, and rapidly quenching the heated portion. Even when a high-strength workpiece is bent, it is possible to effectively obtain a product having excellent shape fixability and uniform hardness distribution at low costs for wide application for bending sophisticated automobile parts.

1 - 5 . (canceled) 
     
     
         6 . A bent product as being subjected to a thermomechanical treatment by virtue of a bending method for three-dimensionally bending a metal material as a workpiece comprising:
 feeding the workpiece by a feeding unit which is provided at an upstream side of the workpiece;   supporting the workpiece by a supporting unit at a downstream side of the feeding unit; and   processing the workpiece by:
 (a) clamping the workpiece with a three-dimensionally movable unit that is provided at a downstream side of the supporting unit; the three-dimensionally movable unit comprising two rolls, three rolls, or four rolls; 
 (b) heating a local part of the workpiece by a heating unit that is provided at an upstream side of the three-dimensionally movable unit in a temperature range which allows quenching to be performed, 
 (c) applying bending moments in three dimensions to said heated local part of the workpiece by the three-dimensionally movable unit in association with the supporting position and/or the moving speed of the workpiece after step (b); and 
 (d) rapidly cooling down the heated portion by a cooling unit that is provided between the heating unit and the three-dimensionally movable unit in order to perform quenching after step (c); 
   the bent product having a tensile strength of 900 MPa or more.   
     
     
         7 . The bent product of  claim 6 , wherein said temperature range of step (b) is over an A 3  transformation point of the metal material as the workpiece. 
     
     
         8 . The bent product of  claim 7 , wherein the cooling rate is more than 100° C./sec in step (d). 
     
     
         9 . The bent product of  claim 8 , wherein the local part of the workpiece to be heated is with a length-wise width of within 30 mm in an axial direction. 
     
     
         10 . The bent product of  claim 6 , wherein the three-dimensionally movable unit is provided with at least one of a shifting mechanism for moving the three-dimensionally movable unit in a vertical direction, a shifting mechanism for moving the three-dimensionally movable unit in a horizontal direction, a tilting mechanism for inclining the three-dimensionally movable unit in a vertical plane, and a tilting mechanism for inclining the three-dimensionally movable unit in a horizontal plane. 
     
     
         11 . The bent product of  claim 6 , wherein the three-dimensionally movable unit is provided with a rotating mechanism for rotating the three-dimensionally movable unit in a circumferential direction.