Rigid foam and associated article and method

Abstract

A rigid polyurethane or polyisocyanurate foam includes 1 to 50 weight percent of a particulate poly(phenylene ether) having a mean particle size of 1 to 40 micrometers. The particulate poly(phenylene ether) imparts reduced flammability and reduced water absorption to the foam. The foam is useful as a thermally insulating material in articles including domestic appliances, building materials, tanks, pipelines, heating pipes, cooling pipes, cold stores, and refrigerated vehicles.

1 . A polyurethane or polyisocyanurate foam comprising 1 to 50 weight percent, based on the total weight of the polyurethane or polyisocyanurate foam, of a particulate poly(phenylene ether) having a mean particle size of 1 to 40 micrometers; wherein the polyurethane or polyisocyanurate foam has a core density of 0.03 to 0.7 grams/centimeter 3  determined at 23° C. using ASTM D 1622-03. 
     
     
         2 . The polyurethane or polyisocyanurate foam of  claim 1 , having a core density of 0.03 to 0.06 grams/centimeter 3  determined at 23° C. using ASTM D 1622-03. 
     
     
         3 . The polyurethane or polyisocyanurate foam of  claim 1 , wherein the polyurethane or polyisocyanurate foam is a polyurethane foam that is the product of a process characterized by an isocyanate index of 105 to 125. 
     
     
         4 . The polyurethane or polyisocyanurate foam of  claim 1 , wherein the polyurethane or polyisocyanurate foam is a polyisocyanurate foam that is the product of a process characterized by an isocyanate index of 180 to 350. 
     
     
         5 . The polyurethane or polyisocyanurate foam of  claim 1 , wherein the particulate poly(phenylene ether) is a particulate poly(2,6-dimethyl-1,4-phenylene ether). 
     
     
         6 . The polyurethane or polyisocyanurate foam of  claim 1 , wherein the particulate poly(phenylene ether) has a mean particle size of 2 to 8 micrometers. 
     
     
         7 . The polyurethane or polyisocyanurate foam of  claim 1 , wherein the particulate poly(phenylene ether) has a particle size distribution wherein 90 volume percent of the particle size distribution is in the range of 1 to 8 micrometers. 
     
     
         8 . The polyurethane or polyisocyanurate foam of  claim 1 , comprising 5 to 30 weight percent of the particulate poly(phenylene ether). 
     
     
         9 . The polyurethane or polyisocyanurate foam of  claim 1 , wherein the polyurethane or polyisocyanurate foam is a product of a method comprising
 reacting a polyol and an isocyanate compound in the presence of a blowing agent and a particulate poly(phenylene ether) to form the polyurethane or polyisocyanurate foam;   wherein the isocyanate compound comprises, on average, at least two isocyanate groups per molecule.   
     
     
         10 . The polyurethane or polyisocyanurate foam of  claim 9 , wherein the polyol comprises an ethoxylated saccharide, a propoxylated saccharide, a butoxylated saccharide, an ethoxylated glycerin, a propoxylated glycerin, a butoxylated glycerin, an ethoxylated diethanolamine, a propoxylated diethanolamine, a butoxylated diethanolamine, an ethoxylated triethanolamine, a propoxylated triethanolamine, a butoxylated triethanolamine, an ethoxylated trimethylolpropane, a propoxylated trimethylolpropane, a butoxylated trimethylolpropane, an ethoxylated erythritol, a propoxylated erythritol, a butoxylated erythritol, an ethoxylated pentaerythritol, a propoxylated pentaerythritol, a butoxylated pentaerythritol, an aliphatic polyester diol, an aromatic polyester polyol, or a combination thereof. 
     
     
         11 . The polyurethane or polyisocyanurate foam of  claim 9 , wherein the polyol comprises a propoxylated sucrose, a propoxylated glycerin, an aromatic polyester diol, or a combination thereof. 
     
     
         12 . The polyurethane or polyisocyanurate foam of  claim 9 , wherein the isocyanate compound comprises 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diisocyanate, 2,2,4-trimethyl-1,6-hexamethylene diisocyanate, 1,12-dodecamethylene diisocyanate, cyclohexane-1,3-diisocyanate, and cyclohexane-1,4-diisocyanate, 1-isocyanato-2-isocyanatomethyl cyclopentane, 1-isocyanato-3-isocyanatomethyl-3,5,5-trimethyl-cyclohexane, bis(4-isocyanatocyclohexyl)methane, 2,4′-dicyclohexyl-methane diisocyanate, 1,3-bis(isocyanatomethyl)-cyclohexane, 1,4-bis-(isocyanatomethyl)-cyclohexane, bis(4-isocyanato-3-methyl-cyclohexyl)methane, alpha,alpha,alpha′,alpha′-tetramethyl-1,3-xylylene diisocyanate, alpha,alpha,alpha′,alpha′-tetramethyl-1,4-xylylene diisocyanate, 1-isocyanato-1-methyl-4(3)-isocyanatomethyl cyclohexane, 2,4-hexahydrotoluene diisocyanate, 2,6-hexahydrotoluene diisocyanate, 1,3-phenylene diisocyanate, 1,4-phenylene diisocyanate, 2,4-toluene diisocyanate, 2,6-toluene diisocyanate, 2,4-diphenylmethane diisocyanate, 4,4′-diphenylmethane diisocyanate, 1,5-diisocyanato naphthalene, an oligomeric diphenylmethane diisocyanate having an average of greater than 2 and less than or equal to 4 isocyanate groups per molecule, or a combination thereof. 
     
     
         13 . The polyurethane or polyisocyanurate foam of  claim 9 , wherein the isocyanate compound comprises an oligomeric diphenylmethane diisocyanate having an average of greater than 2 and less than or equal to 4 isocyanate groups per molecule. 
     
     
         14 . The polyurethane or polyisocyanurate foam of  claim 1 ,
 wherein the polyurethane or polyisocyanurate foam has a core density of 0.02 to 0.06 grams/centimeter 3  determined at 23° C. using ASTM D 1622-03;   wherein the particulate poly(phenylene ether) is a particulate poly(2,6-dimethyl-1,4-phenylene ether);   wherein the particulate poly(phenylene ether) has a mean particle size of 2 to 8 micrometers;   wherein the particulate poly(phenylene ether) has a particle size distribution wherein 90 percent of the particle volume distribution is in the range of 1 to 8 micrometers;   wherein the polyurethane or polyisocyanurate foam comprises 5 to 30 weight percent of the particulate poly(phenylene ether);   wherein the polyurethane or polyisocyanurate foam is a product of a method comprising
 reacting a polyol and an isocyanate compound in the presence of a blowing agent and a particulate poly(phenylene ether) to form the polyurethane or polyisocyanurate foam, 
 wherein the isocyanate compound comprises, on average, at least two isocyanate groups per molecule; 
   wherein the polyol comprises a wherein the polyol comprises a propoxylated sucrose, a propoxylated glycerin, an aromatic polyester diol, or a combination thereof; and   wherein the isocyanate compound comprises an oligomeric diphenylmethane diisocyanate having an average of greater than 2 and less than or equal to 4 isocyanate groups per molecule.   
     
     
         15 . An article comprising thermal insulation comprising polyurethane or polyisocyanurate foam comprising 1 to 50 weight percent, based on the total weight of the polyurethane or polyisocyanurate foam, of a particulate poly(phenylene ether) having a mean particle size of 1 to 40 micrometers; wherein the polyurethane or polyisocyanurate foam has a core density of 0.03 to 0.7 grams/centimeter 3  determined at 23° C. using ASTM D 1622-03. 
     
     
         16 . A method of forming a polyurethane or polyisocyanurate foam, the method comprising:
 reacting a polyol and an isocyanate compound in the presence of a blowing agent and a particulate poly(phenylene ether) to form a polyurethane or polyisocyanurate foam;   wherein the isocyanate compound comprises, on average, at least two isocyanate groups per molecule;   wherein the particulate poly(phenylene ether) has a mean particle size of 1 to 40 micrometers; and   wherein the polyurethane or polyisocyanurate foam comprises 1 to 50 weight percent of the particulate poly(phenylene ether).   
     
     
         17 . The method of  claim 16 , wherein the polyol, the isocyanate compound, and water, if any, are present in amounts sufficient to provide an isocyanate index of 180 to 350. 
     
     
         18 . The method of  claim 16 ,
 wherein the polyurethane or polyisocyanurate foam has a core density of 0.02 to 0.06 grams/centimeter 3  determined at 23° C. using ASTM D 1622-03;   wherein the particulate poly(phenylene ether) is a particulate poly(2,6-dimethyl-1,4-phenylene ether);   wherein the particulate poly(phenylene ether) has a mean particle size of 2 to 8 micrometers;   wherein the particulate poly(phenylene ether) has a particle size distribution wherein 90 percent of the particle volume distribution is in the range of 1 to 8 micrometers;   wherein the polyurethane or polyisocyanurate foam comprises 5 to 30 weight percent of the particulate poly(phenylene ether);   wherein the polyol comprises a propoxylated sucrose, a propoxylated glycerin, an aromatic polyester diol, or a combination thereof, and   wherein the isocyanate compound comprises an oligomeric diphenylmethane diisocyanate having an average of greater than 2 and less than or equal to 4 isocyanate groups per molecule.