Fire proof oriented strand board and its manufacture

Abstract

The invention pertains to a method of manufacturing a fire proof board from strands of wood, the method comprising the following steps in the given order: (a) providing strands of wood, (b) immersing the strands of wood in a watery solution of a flame retardant chemical composition, (c) separating the strands of wood from each other, (d) at least in part drying the strands of wood, (e) applying an adhesive to the strands of wood, and (f) forming a board of a predetermined shape from the strands. The invention furthermore pertains to a board formed by a plurality of strands of wood that are compressed and bonded together with an adhesive, wherein the board further comprises a flame retardant chemical composition, said composition comprising a phosphate compound.

1 . A method of manufacturing a fire proof board from strands of wood, the method comprising the following steps in the given order:
 (a) providing strands of wood, and then
 measuring whether the provided strands of wood have the desired humidity of between 5% and 25%, preferably between 5% and 20%, even more preferably between 8% and 20%, and then 
 increasing the humidity of the strands if the measurement shows that they have a humidity that is lower than the desired one, or pre-drying the strands, if the measurement shows that they have a humidity that is larger than the desired one, 
   (b) immersing the strands of wood in a watery solution of a flame retardant chemical composition,   (c) separating the strands of wood from each other,   (d) at least in part drying the strands of wood,   (e) applying an adhesive to the strands of wood, and   (f) forming a board of a predetermined shape from the strands.   
     
     
         2 . The method according to  claim 1 , wherein the step (c) of separating the strands from each other is performed substantially simultaneously to the step (b) of immersing the strands in a watery solution of a flame retardant chemical composition, 
     
     
         3 . The method according to  claim 2 , wherein the step (c) of separating the strands from each other comprises stirring the mixture of strands and watery solution of a flame retardant chemical composition. 
     
     
         4 . The method according to  claim 1 , wherein the step (d) of drying the strands of wood comprises the step of drying the strands of wood to a humidity of between 4% and 10%, preferably between 4% and 8%, such as for example about 6%. 
     
     
         5 . The method according to  claim 1 , wherein the step (d) of drying the strands of wood comprises the step of drying the strands for 2 minutes-10 minutes, preferably for 2 minutes-8 minutes, even more preferably for 2 minutes-6 minutes, yet even more preferably for 3 minutes-4 minutes. 
     
     
         6 . The method according to  claim 1 , wherein the watery solution of the fire retardant chemical composition comprises an unsaturated solution of said chemical composition. 
     
     
         7 . The method according to  claim 1 , wherein the watery solution of the fire retardant chemical composition comprises less than 25% by weight of said solution, preferably between 15% and 22%, such as 18.5% by weight of said solution. 
     
     
         8 . The method according to  claim 1 , wherein the step (b) of immersing the strands of wood in a watery solution of a flame retardant chemical composition comprises the sub step of immersing the strands of wood in a watery solution of a flame retardant chemical composition for less than 10 minutes on average, preferably between 2 minutes and 6 minutes, even more preferably between 3 minutes and 4 minutes. 
     
     
         9 . The method according to  claim 1 , wherein the step (f) further comprises the sub steps of
 aligning the strands so that they are substantially parallel to each other,   compressing the aligned strands and adhesive with pressure into a predetermined shape, and   curing said compressed mixture of strands and adhesive to produce a board of strands having a predetermined shape.   
     
     
         10 . The method according to  claim 1 , wherein the step (f) further comprises the sub steps of
 forming at least two layers of strands, wherein the strands of each layer are substantially parallel to each other,   placing the layers on top of each other in such a way that the strands of two abutting layers are not parallel to each other,   compressing the layers of strands and adhesive with pressure into a predetermined shape, and   curing said compressed mixture of strands and adhesive to produce a layered board of strands having a predetermined shape.   
     
     
         11 . The method according to  claim 1 , wherein the step (f) further comprises the sub steps of
 compressing the strands and adhesive with pressure into a predetermined shape, and   curing said compressed mixture of strands and adhesive to produce a board of strands having a predetermined shape.   
     
     
         12 . The method according to  claim 1 , wherein the step (d) of drying the strands of wood comprises the step of
 subjecting the strands of wood to an air-jet, which has a direction that is substantially opposite to the force of gravity on the strands.   
     
     
         13 . The method according to  claim 1 , wherein the step (e) of applying an adhesive to the strands of wood, comprises the sub step of spraying the adhesive on the strands of wood and/or placing the strands of wood in the adhesive. 
     
     
         14 . The method according to  claim 1 , wherein the flame retardant chemical composition comprises a phosphate compound. 
     
     
         15 . The method according to  claim 1 , wherein the flame retardant chemical composition comprises a pH regulating compound. 
     
     
         16 . The method according to  claim 1 , wherein the flame retardant chemical composition comprises a preservative compound. 
     
     
         17 . The method according to  claim 14 , wherein the phosphate compound is an ammonium phosphate. 
     
     
         18 . The method according to  claim 15 , wherein the pH regulating compound is a weak organic acid. 
     
     
         19 . The method according to  claim 16 , wherein the preservative compound is a source of benzoate ion. 
     
     
         20 . The method according to  claim 14 , wherein phosphate compound forms between 5% and 30% by weight of the flame retardant chemical composition. 
     
     
         21 . The method according to  claim 14 , wherein pH regulating compound forms between 0.25% and 10% by weight of the flame retardant chemical composition. 
     
     
         22 . The method according to  claim 14 , wherein preservative compound forms between 0.25% and 15% by weight of the flame retardant chemical composition. 
     
     
         23 . The method according to  claim 1 , wherein the flame retardant chemical compound comprises in a mixture: ammonium phosphate, a source of citrate ion, a source of benzoate ion, wherein there is 1 part by weight of the source of citrate ion, 12.7 to 20 parts by weight of ammonium phosphate, and 0.8 to 2.2 parts by weight of the source of benzoate ion. 
     
     
         24 - 38 . (canceled)