Method for manufacturing fiber fabric, and fiber fabric

Abstract

A method for manufacturing a fiber fabric having a hard handle is provided without using, in particular, thick yarns, manufacturing a fabric in the high density which increases loads at stages of composing and organizing the fabric, or performing resin treatment for hard finishing. The method includes performing treatment on a fabric mainly including nylon fibers with a treatment liquid containing benzyl alcohol. The treatment with the treatment liquid is performed so that the fiber fabric has a bending resistance of 100 mm or higher in at least one of a warp direction and a weft direction as measured according to a 45-degree cantilever method specified in

1 . A method for manufacturing a fiber fabric, comprising
 performing treatment on a fabric mainly including nylon fibers with a treatment liquid containing benzyl alcohol.   
     
     
         2 . The method for manufacturing a fiber fabric according to  claim 1 ,
 wherein the treatment with the treatment liquid is performed so that the fiber fabric has a bending resistance of 100 mm or higher in at least one of a warp direction and a weft direction as measured according to a 45-degree cantilever method specified in JIS L 1096.   
     
     
         3 . The method for manufacturing a fiber fabric according to  claim 1 ,
 wherein the treatment liquid contains water and 10 grams or more of the benzyl alcohol per litter of the treatment liquid.   
     
     
         4 . The method for manufacturing a fiber fabric according to  claim 1 ,
 wherein the fabric including the nylon fibers is in rope form, and   the treatment with the treatment liquid is performed at a temperature from 80 degrees Celsius to 130 degrees Celsius.   
     
     
         5 . The method for manufacturing a fiber fabric according to  claim 1 ,
 wherein the fabric including the nylon fibers is in open width form, and   the treatment with the treatment liquid is performed at a temperature from 80 degrees Celsius to 130 degrees Celsius.   
     
     
         6 . The method for manufacturing a fiber fabric according to  claim 1 ,
 wherein the fabric made only of the nylon fibers.   
     
     
         7 . A fiber fabric obtained by performing treatment on a fabric mainly including nylon fibers with a treatment liquid containing benzyl alcohol. 
     
     
         8 . The fiber fabric according to  claim 7 ,
 wherein the fiber fabric resulting from the treatment with the treatment liquid has a bending resistance of 100 mm or higher in at least one of a warp direction and a weft direction as measured according to a 45-degree cantilever method specified in JIS L 1096.   
     
     
         9 . The fiber fabric according to  claim 7 ,
 wherein the fabric made only of the nylon fibers.   
     
     
         10 . A garment including the fiber fabric according to  claim 7 . 
     
     
         11 . A storage tool including the fiber fabric according to  claim 7 .