Gas barrier multilayer film

Abstract

A film which can be industrially coated easily and exhibits excellent gas barrier performance without being subjected to a high-temperature heat treatment, good gas barrier performance immediately after the production, and maintains the excellent gas barrier performance while exhibiting excellent hot water resistance and printing resistance; a gas barrier laminated film including a resin layer on an inorganic thin film formed on at least one surface of a support film, the resin layer being formed by applying: (1) an aqueous dispersion containing polyvinyl alcohol (a), an ethylene-unsaturated carboxylic acid copolymer (b), and inorganic particles (c); (2) an aqueous dispersion containing an ethylene-unsaturated carboxylic acid copolymer (b), inorganic particles (c), and/or a cross-linking agent (d); or (3) an aqueous dispersion containing polyvinyl alcohol (a), an ethylene-unsaturated carboxylic acid copolymer (b), inorganic particles (c), and cross-linking agent (d), to the inorganic thin film surface; and a method of producing the gas barrier laminated film.

1 . A gas barrier laminated film comprising a thermoplastic polymer film, an inorganic thin film which is formed on at least one side of the thermoplastic polymer film, and a resin layer which is obtained by applying an aqueous dispersion containing an ethylene-unsaturated carboxylic acid copolymer (b) and inorganic particles (c), to a surface of the inorganic thin film, wherein an average particle diameter of the inorganic particles (c) is 0.5 to 25 nm and the inorganic particles (c) are silica particles having a silanol group. 
     
     
         2 . A gas barrier laminated film comprising a thermoplastic polymer film, an inorganic thin film which is formed on at least one side of the thermoplastic polymer film, and a resin layer which is obtained by applying an aqueous dispersion containing an ethylene-unsaturated carboxylic acid copolymer (b) and a cross-linking agent (d), to a surface of the inorganic thin film. 
     
     
         3 . The gas barrier laminated film according to  claim 1 , wherein the aqueous dispersion comprises polyvinyl alcohol (a), the ethylene-unsaturated carboxylic acid copolymer (b) and the inorganic particles (c). 
     
     
         4 . The gas barrier laminated film according to  claim 1  or  3 , wherein the aqueous dispersion further comprises a cross-linking agent (d). 
     
     
         5 . The gas barrier laminated film according to  claim 3 , wherein a degree of saponification of the polyvinyl alcohol (a) is 90% or more. 
     
     
         6 . The gas barrier laminated film according to  claim 1  or  2 , wherein the ethylene-unsaturated carboxylic acid copolymer (b) contains a neutralized substance of ethylene-unsaturated carboxylic acid copolymer. 
     
     
         7 . The gas barrier laminated film according to  claim 6 , wherein the neutralized substance of ethylene-unsaturated carboxylic acid copolymer includes alkaline metal salt of ethylene-unsaturated carboxylic acid copolymer. 
     
     
         8 . The gas barrier laminated film according to  claim 2 , wherein the cross-linking agent (d) contains at least one member selected from an oxazoline group, a carbodiimide group, an epoxy group, and an isocyanate group. 
     
     
         9 . The gas barrier laminated film according to  claim 3 , wherein, in the resin layer, at least one of the following contents is satisfied:
 a content of the polyvinyl alcohol (a) being 10 to 95 mass % with respect to a total amount based on solid content of the component (a), the component (b), and the component (c);   a content of the ethylene-unsaturated carboxylic acid copolymer (b) being 3 to 80 mass % with respect to a total amount based on solid content of the component (a), the component (b), and the component (c); and   a content of the inorganic particles (c) being 2 to 80 mass % with respect to a total amount based on solid content of the component (a), the component (b), and the component (c).   
     
     
         10 . The gas barrier laminated film according to  claim 4 , wherein, in the resin layer, at least one of the following contents is satisfied:
 a content of the inorganic particles (c) being 5 to 75 mass % with respect to a total amount based on solid content of the component (b), the component (c), and the component (d); and   a content of the cross-linking agent (d) being 3 to 50 mass % with respect to a total amount based on solid content of the component (b), the component (c), and the component (d).   
     
     
         11 . The gas barrier laminated film according to  claim 4 , wherein, in the resin layer, at least one of the following contents is satisfied:
 a content of polyvinyl alcohol (a) being 5 to 70 mass % with respect to a total amount based on solid content of the component (a), the component (b), the component (c), and the component (d);   a content of ethylene-unsaturated carboxylic acid copolymer (b) being 10 to 70 mass % with respect to a total amount based on solid content of the component (a), the component (b), the component (c), and the component (d);   a content of the inorganic particles (c) being 20 to 70 mass % with respect to a total amount based on solid content of the component (a), the component (b), the component (c), and the component (d); and   a content of the cross-linking agent (d) being 2 to 30 mass % with respect to a total amount based on solid content of the component (a), the component (b), the component (c), and the component (d).   
     
     
         12 . The gas barrier laminated film according to  claim 3 , wherein a content ratio of the polyvinyl alcohol (a) and the ethylene-unsaturated carboxylic acid copolymer (b) is 95:5 to 25:75 in a mass ratio. 
     
     
         13 . The gas barrier laminated film according to  claim 3 , wherein, in the resin layer, at least one of the content ratios (i) to (iii) is satisfied:
 (i) a content ratio [(a)/(b)] of the polyvinyl alcohol (a) and the ethylene-unsaturated carboxylic acid copolymer (b) being 90/10 to 5/95 in a mass ratio;   (ii) a content ratio of [((a)+(b))/(c)] of the inorganic particles (c) with respect to a total amount of the polyvinyl alcohol (a) and the ethylene-unsaturated carboxylic acid copolymer (b) being 25/75 to 90/10 in a mass ratio; and   (iii) a content ratio of [(b)/(d)] of the ethylene-unsaturated carboxylic acid copolymer (b) and the cross-linking agent (d) being 98/2 to 40/60 in a mass ratio.   
     
     
         14 . The gas barrier laminated film according to  claim 1  or  2 , wherein a thickness of the resin layer is 0.05 to 10 μm. 
     
     
         15 . The gas barrier laminated film according to  claim 1  or  2 , further comprising an anchor coat layer between the thermoplastic polymer film and the inorganic thin film. 
     
     
         16 . The gas barrier laminated film according to  claim 15 , wherein the anchor coat layer contains at least one member selected from a polyester resin, an urethane resin, an acrylic resin, an oxazoline group-containing resin, a carbodiimide group-containing resin, an epoxy group-containing resin, an isocyanate group-containing resin, and their copolymers. 
     
     
         17 . The gas barrier laminated film according to  claim 1  or  2 , wherein the inorganic thin film comprises at least one member selected from a silicon oxide, an aluminum oxide, and a hydrocarbon. 
     
     
         18 . The gas barrier laminated film according to  claim 1  or  2 , wherein the thermoplastic polymer film comprises at least one member selected from polyester, polyamide, and polyvinyl alcohol. 
     
     
         19 . A method for producing a gas barrier laminated film, comprising:
 (A) forming an inorganic thin film by vacuum deposition on at least one side of a thermoplastic polymer film; and   (B) applying, to a surface of the inorganic thin film, an aqueous dispersion containing an ethylene-unsaturated carboxylic acid copolymer (b), and silica particles having a silanol group (c) and/or a cross-linking agent (d),   wherein an average particle diameter of the silica particles (c) is 0.5 to 25 nm.   
     
     
         20 . The method for producing a gas barrier laminated film according to  claim 19 , wherein the aqueous dispersion comprises polyvinyl alcohol (a), the ethylene-unsaturated carboxylic acid copolymer (b) and the silica particles (c); and the aqueous dispersion is obtained by mixing the polyvinyl alcohol (a), the ethylene-unsaturated carboxylic acid copolymer (b), and the silica particles (c). 
     
     
         21 . The method for producing a gas barrier laminated film according to  claim 19 , wherein the aqueous dispersion comprises polyvinyl alcohol (a), the ethylene-unsaturated carboxylic acid copolymer (b), the silica particles (c) and a cross-linking agent (d), and the aqueous dispersion is obtained by mixing the polyvinyl alcohol (a), the ethylene-unsaturated carboxylic acid copolymer (b), the silica particles (c) and the cross-linking agent (d). 
     
     
         22 . The method for producing a gas barrier laminated film according to  claim 19 , wherein heat treatment is performed at 60° C. or higher after the formation of the inorganic thin film, after the formation of the resin layer, or both after the formation of the inorganic thin film and the formation of the resin layer. 
     
     
         23 . A gas barrier laminate, wherein at least one member selected from plastic films and paper is laminated on the laminated film according to  claim 1  or  2 . 
     
     
         24 . The gas barrier laminate according to  claim 23 , comprising:
 a thermoplastic polymer film including a biaxially stretched polyester film; and   an oxygen permeability after performing hot water treatment at 95° C. for 30 minutes of 30 cc/m 2 /24 hr/MPa or less;   the laminate being obtained by laminating a 30 to 200 μm thick unstretched polypropylene film to a surface of the resin layer of the laminated film or successively laminating a 5 to 10 μm thick biaxially stretched nylon 6 film and the 30 to 200 μm thick unstretched polypropylene film to a surface of the resin layer of the laminated film.   
     
     
         25 . The gas barrier laminate according to  claim 23 , comprising:
 a thermoplastic polymer film including a biaxially stretched polyester film; and   an oxygen permeability after performing hot water treatment at 120° C. for 30 minutes of 20 cc/m 2 /24 hr/MPa (10 fmol/m 2 /s/Pa) or less,   the laminate being obtained by laminating a 30 to 200 μm thick unstretched polypropylene film to a surface of the resin layer of the laminated film or successively laminating a 5 to 10 μm thick biaxially stretched nylon 6 film and the 30 to 200 μm thick unstretched polypropylene film to a surface of the resin layer of the laminated film.   
     
     
         26 . The gas barrier laminate according to  claim 23 , comprising:
 a thermoplastic polymer film including a biaxially stretched polyamide film; and   an oxygen permeability after performing hot water treatment at 95° C. for 30 minutes of 20 cc/m 2 /24 hr/MPa or less,   the laminate being obtained by laminating a 5 to 10 μm thick biaxially stretched polyester film to a surface side of the resin layer of the laminated film and laminating a 30 to 200 μm thick unstretched polypropylene film to a surface side of the thermoplastic polymer film.   
     
     
         27 . The gas barrier laminate according to  claim 23 , comprising:
 a thermoplastic polymer film including a biaxially stretched polyamide film; and   an oxygen permeability after performing hot water treatment at 120° C. for 30 minutes of 20 cc/m 2 /24 hr/MPa or less,   the laminate being obtained by laminating a 5 to 10 μm thick biaxially stretched polyester film to a surface side of the resin layer of the laminated film and laminating a 30 to 200 μm thick unstretched polypropylene film to a surface side of the thermoplastic polymer film.   
     
     
         28 . The gas barrier laminated film according to  claim 1 , wherein the average particle diameter of the inorganic particles (c) has an upper limit of 10 nm. 
     
     
         29 . The gas barrier laminated film according to  claim 1 , wherein the average particle diameter of the inorganic particles (c) has an upper limit of 5 nm. 
     
     
         30 . The gas barrier laminated film according to  claim 4 , wherein the cross-linking agent (d) contains at least one member selected from an oxazoline group, a carbodiimide group, an epoxy group, and an isocyanate group.