Refractory lining for titanium ore beneficiation

Abstract

The disclosure relates to a refractory which is resistant to corrosion which degrades the refractory during titanium-ore beneficiation in a furnace, particularly a rotary hearth furnace. In particular, the disclosure relates to a layered refractory lining for a furnace, for use in a titanium ore beneficiation process wherein a titanium oxide-rich molten slag is formed, comprising: (a) a first layer comprising a major proportion of alumina and a minor proportion of zirconia; (b) a second layer comprising a resistant agent for the molten slag; wherein the second layer is between the slag and the first layer.

1 - 13 . (canceled) 
     
     
         14 . A process for forming a resistant agent in a refractory body of a furnace for use in a titanium ore beneficiation process, comprising:
 (i) forming agglomerates comprising carbon-based materials and a titanium-bearing ore, the quantity of carbon of the agglomerates being sufficient for, at an elevated temperature, reducing ferric oxide to ferrous oxide and forming a slag that is comprised of titanium oxide and iron oxide;   (ii) introducing the agglomerates onto a carbon bed of a moving hearth furnace, wherein the moving hearth furnace comprises a refractory lining comprising a first layer comprising alumina and zirconia having about 90 to about 99 wt. % alumina, and about 1 to about 10 wt. % zirconia, based on the entire weight of the first layer;   (iii) heating the agglomerates in the moving hearth furnace to a temperature sufficient for reducing and melting the agglomerates to produce a titanium oxide-rich molten slag, which contacts the refractory lining to produce a second layer comprising a resistant agent which is a reaction product of the slag, the alumina and the zirconia; wherein the second layer is formed between the slag and the first layer; and   wherein the total amount of calcium oxide, magnesium oxide, yttrium oxide and cerium oxide is less than 1 wt. %, based on the total weight of the refractory body.   
     
     
         15 . A resistant agent for a titanium oxide-rich molten slag comprising a reaction product of a first layer of a refractory lining comprising alumina and zirconia having about 90 to about 99 wt. % alumina, and about 1 to about 10 wt. % zirconia, based on the entire weight of the first layer
 and the titanium oxide-rich molten slag, wherein the resistant agent is the reaction product of the titanium oxide of the slag and the alumina and zirconia of the first layer; and   wherein the total amount of calcium oxide, magnesium oxide, yttrium oxide and cerium oxide is less than 1 wt. %, based on the total weight of the refractory body.