Transparentization agent composition containing sorbitol compound and method for producing polypropylene resin composition using this sorbitol compound

Abstract

A transparentization agent composition is a mixture containing 100 parts by mass of a dibenzylidene sorbitol compound represented by a general formula (I) having a particle diameter such that d 97 is from 30 μm to 200 μm and 5 to 200 parts by mass of tetrakis[3(3,5-di-tert-butyl-4-hydroxyphenyl)propionyloxymethyl]methane, wherein the total for the two components is 50% by mass or more of the mixture. Also disclosed is a method for producing a polypropylene resin composition, including obtaining a polypropylene resin composition in which a dibenzylidene sorbitol compound represented by a general formula (I) having a particle diameter such that d 97 is from 30 μm to 200 μm is incorporated in a polypropylene resin, by kneading a mixture containing 100 parts by mass of the polypropylene resin and 0.05 to 2 parts by mass of the dibenzylidene sorbitol compound by using a biaxial extruder at an extrusion temperature of from 220 to 250° C.

1 . A transparentization agent composition, which is a mixture containing 100 parts by mass of a dibenzylidene sorbitol compound represented by the following general formula (I) having a particle diameter such that d 97  is from 30 μm to 200 μm and 5 to 200 parts by mass of tetrakis[3(3,5-di-tert-butyl-4-hydroxyphenyl)propionyloxymethyl]methane, wherein the total for the two components is 50% by mass or more of the mixture. 
       
         
           
           
               
               
           
         
       
     
     
         2 . The transparentization agent composition according to  claim 1 , wherein the dibenzylidene sorbitol compound represented by the general formula (I) has d 97  of from 40 μm to 100 μm. 
     
     
         3 . A method for producing a polypropylene resin composition, comprising obtaining a polypropylene resin composition in which a dibenzylidene sorbitol compound represented by the following general formula (I) having a particle diameter such that d 97  is from 30 μm to 200 μm is incorporated in a polypropylene resin, by kneading a mixture containing 100 parts by mass of the polypropylene resin and 0.05 to 2 parts by mass of the dibenzylidene sorbitol compound by using a biaxial extruder at an extrusion temperature of from 220 to 250° C. 
       
         
           
           
               
               
           
         
       
     
     
         4 . The method for producing a polypropylene resin composition according to  claim 3 , wherein the dibenzylidene sorbitol compound represented by the general formula (I) has d 97  of from 40 μm to 150 μm. 
     
     
         5 . The method for producing a polypropylene resin composition according to  claim 3 , wherein the biaxial extruder comprises at least three temperature-controlled areas from a resin injection part to dies, and the temperatures of the parts other than the resin injection part and other than the dies are each set to 220 to 250° C. 
     
     
         6 . The method for producing a polypropylene resin composition according to  claim 4 , wherein the biaxial extruder comprises at least three temperature-controlled areas from a resin injection part to dies, and the temperatures of the parts other than the resin injection part and other than the dies are each set to 220 to 250° C.