Titanium dioxide photocatalyst containing carbon and method for its production

Abstract

The invetion relates to a titanium dioxide-based photocatalyst containing carbon that is highly photoactive in visible light (vlp-TiO 2 ) and to a method of manufacture. The vlp-TiO 2 is manufactured by mixing a fine grained titanium compount (BET≧50 m 2 /g) with an organic carbon compound and subsequent thermal treatment at temperatures up to 350° C. The carbon content amounts to 0.05 to 4% by weight, preferably 0.4 to 0.8% by weight. The product is characterized by an ESR spectrum which displays only one significant signal in the g value range from 1.97 to 2.05 at g about 2.003. The inventive photocatalyst can be used for to degrade contaminants and pollutants in liquids and gases.

1 - 24 . (canceled) 
     
     
         25 . A material, comprising;
 a photocatalyst based on carbon containing titanium dioxide particles, wherein the material shows significant light absorption for light of wavelength λ>400 nm compared to pure titanium dioxide particles, wherein the carbon content is in the range from 0.05 to 4% by weight, and wherein the carbon content of the TiO 2  particles is only embedded in a surface layer of the TiO 2  particles.   
     
     
         26 . The material of  claim 25 , wherein the Kubelka-Munk function F(R∞), which is proportional to the absorbancy, at 500 nm is roughly 50% the value at 400 nm, and at 600 nm is roughly 20% of the value at 400 nm. 
     
     
         27 . The material of  claim 26 , wherein the specific surface area of the material according to BET is 100 to 250 m 2 /g. 
     
     
         28 . The material of  claim 27 , wherein the material is characterized by a strong absorption band at a bond energy of 285.6 eV in the X-ray photoelectron spectrum (XPS), referred to the O(1s) band at 530 eV. 
     
     
         29 . The material of  claim 25 , wherein the Kubelka-Munk function F(R 4), which is proportional to the absorbancy, at 500 nm is roughly 50% the value at 400 nm, and at 600 nm is roughly 20% of the value at 400 nm. 
     
     
         30 . The material of  claim 25 , wherein the photoactivity is at least 20%. 
     
     
         31 . The material of  claim 30 , wherein the photoactivity is at least 40%. 
     
     
         32 . The material of  claim 25 , wherein the carbon content is in the range from 0.05 to 2% by weight. 
     
     
         33 . The material of  claim 32 , wherein the carbon content is in the range from 0.3 to 1.5% by weight. 
     
     
         34 . The material of  claim 33 , wherein the carbon content is in the range from 0.4 to 0.8% by weight. 
     
     
         35 . The material of  claim 25 , wherein the specific surface area of the material according to BET is 100 to 250 m 2 /g. 
     
     
         36 . The material of  claim 25 , wherein the material does not display significant carbonate bands, either in the X-ray photoelectron spectrum or in the infrared spectrum. 
     
     
         37 . The material of  claim 25 , wherein the material is incorporated into materials chosen from the group consisting of plastics, plastic sheeting, fibers, paper, and road surfacing material. 
     
     
         38 . The material of  claim 25 , wherein the material is incorporated into construction materials chosen from the group consisting of prefabricated concrete elements, concrete paving stones, roof tiles, ceramics, decorative tiles, wallpapers, fabrics, and panels and cladding elements for ceilings and walls in indoor and outdoor areas. 
     
     
         39 . The material of  claim 25 , wherein the material is incorporated in devices for air purification and air sterilization and for water purification especially for antibacterial and antiviral purposes. 
     
     
         40 . The material of  claim 25 , wherein the material is incorporated in photovoltaic cells and in devices for photolysis. 
     
     
         41 . The material of  claim 25 , wherein the specific surface of the material is greater than 100 m 2 /g. 
     
     
         42 . A material, comprising;
 a photocatalyst based on carbon containing titanium dioxide particles, wherein the material shows significant light absorption for light of wavelength λ>400 nm compared to pure titanium dioxide particles, and wherein the material does not display significant carbonate bands, either in the X-ray photoelectron spectrum or in the infrared spectrum, wherein the carbon content is in the range from 0.05 to 4% by weight, and wherein the carbon content of the TiO 2  particles is only embedded in a surface layer of the TiO 2  particles.   
     
     
         41 . The material of  claim 42 , wherein the material is characterized by an electron spin resonance (ESR) spectrum, measured at a temperature of 5 K, which displays only one significant signal in the g value range from 1.97 to 2.05. 
     
     
         43 . The material of  claim 41 , wherein the one significant signal in the ESR spectrum occurs at a g value of 2.002 to 2.004.