Glove

Abstract

The invention relates to a glove made from a covalently cross-linked elastomer film, which elastomer film contains at least one layered silicate.

1 . Glove made from a covalently cross-linked elastomer film, which elastomer film contains at least one filler, wherein the filler is a layered silicate. 
     
     
         2 . Glove according to  claim 1 , wherein the elastomer film, having a layer thickness of 1 mm, has a permeation resistance in accordance with DIN EN 374-3 of at least 14 minutes before the solvent isopropanol is broken down. 
     
     
         3 . Glove according to  claim 1 , wherein the at least one filler is a clay mineral. 
     
     
         4 . Glove according to  claim 3 , wherein the clay mineral is selected from a group comprising kaolinite, dickite, nacrite, halloysite, allophane, imogolite 
     
     
         5 . Glove according to  claim 3 , wherein the clay mineral is kaolin and/or talcum. 
     
     
         6 . Glove according to  claim 5 , wherein the kaolin contains at least 70% by weight of kaolinite. 
     
     
         7 . Glove according to  claim 3 , wherein the clay mineral is hard-calcinated. 
     
     
         8 . Glove according to  claim 1 , wherein the filler is used in a proportion selected from a range with a lower limit of 5 phr and an upper limit of 30 phr. 
     
     
         9 . Glove according to  claim 1 , wherein the filler is in particulate form and 50% of the particles have a particle diameter of at most 10 μm. 
     
     
         10 . Glove according to  claim 9 , wherein the particle diameter of the biggest particle is at most 30 μm. 
     
     
         11 . Glove according to  claim 1 , wherein the filler has a volume-specific surface of at most 40 m 2 /cm 3 , measured by the BET method. 
     
     
         12 . Glove according to  claim 1 , wherein the elastomer film is made from natural rubber latex. 
     
     
         13 . Glove according to  claim 1 , wherein the elastomer film comprises a single layer. 
     
     
         14 . Method of producing a glove according to  claim 1  by immersing a glove mold in an immersing bath containing latex, which latex contains at least one filler, wherein a layered silicate is used as the filler and the filler is converted into an aqueous dispersion before being added to the latex. 
     
     
         15 . Method according to  claim 14 , wherein the dispersion is added to the latex prior to the initial cross-linking process. 
     
     
         16 . Method according to  claim 14 , wherein the initial cross-linking process is run to a degree of cross-linking degree of at most 96% (swelling of the toluene). 
     
     
         17 . Method of producing an elastomer, comprising:
 supplying a layered silicate as a filler to an elastomer,   wherein a glove formed from a film of the elastomer has the layered silicate filler.   
     
     
         18 . Method according to  claim 17 , wherein the layered silicate comprises kaolin.