Production Of Non-Woven Materials From Polyhydroxyalkanoate

Abstract

Methods and compositions for making non-woven materials from polyhydroxyalkanoate polymers are provided. In certain aspects, the invention pertains to an extruded fiber comprising a polyhydroxyalkanoate polymer, a wet milled nucleating agent and a plasticizer, wherein the average particle size of the wet-milled nucleating agent is about 20 microns and is dispersed in the polymer.

1 . An extruded and melt-blown fiber, comprising a polyhydroxyalkanoate polymer, a wet milled nucleating agent and a plasticizer, wherein the average particle size of the wet-milled nucleating agent is below about 20 microns and is dispersed in the polymer. 
     
     
         2 . The fiber of  claim 1 , wherein the nucleating agent is boron nitride. 
     
     
         3 . The fiber of  claim 1 , wherein the fiber comprises about 75% to about 95% by weight polyhydroxyalkanoate polymer. 
     
     
         4 . The fiber of  claim 1  wherein the fiber has a weight-average molecular weight of at least about 150 kg/mol. 
     
     
         5 . The fiber of  claim 1 , wherein the plasticizer is acetyl tri-n-butyl citrate. 
     
     
         6 . The fiber of  claim 1 , wherein the fiber diameter is about 0.1 to about 50 microns. 
     
     
         7 . The fiber of  claim 1 , wherein the fiber diameter is about 2 to about 5 microns. 
     
     
         8 . The fiber of  claim 1 , wherein the nucleating agent is between about 1% to 10% weight of the total composition. 
     
     
         9 . The fiber of  claim 1 , wherein the basis weight is from about 20 to about 160 GSM. 
     
     
         10 . The fiber of  claim 1 , wherein, the polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate), a poly(3-hydroxybutyrate-co-3-hydroxyvalerate), a poly(3-hydroxybutyrate-co-5-hydroxyvalerate), or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate). 
     
     
         11 . The fiber of  claim 1 , wherein the polyhydroxyalkanoate polymer is a poly(3-hydroxybutyrate) homopolymer, a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content, a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with 5% to 22% 3-hydroxyvalerate content, a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with 5% to 15% 5-hydroxyvalerate content, or a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with 3% to 15% 3-hydroxyhexanoate content. 
     
     
         12 . The fiber of  claim 1 , wherein the polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate). 
     
     
         13 . The fiber of  claim 1 , wherein the polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content. 
     
     
         14 . The fiber of  claim 12 , wherein the polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended to with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); or a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b). 
     
     
         15 . The fiber of  claim 12 , wherein the weight of polymer a) is 20% to 60% of the combined weight of polymer a) and polymer b) and the weight of polymer b) is 40% to 80% of the combined weight of polymer a) and polymer b). 
     
     
         16 . The fiber of  claim 1 , wherein the polyhydroxyalkanoate is a) poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content; a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate; or a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content. 
     
     
         17 . The fiber of  claim 1 , wherein the polyhydroxyalkanoate is a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate) homopolymer blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 5% to 15% 4-hydroxybutyrate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyvalerate) with a 5% to 22% 3-hydroxyvalerate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20-50% 4-hydroxybutyrate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b); or a) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 3% to 15% 3-hydroxyhexanoate content blended with b) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) having a 5%-50% 3-hydroxyhexanoate content and the weight of polymer a) is 5% to 95% of the combined weight of polymer a) and polymer b). 
     
     
         18 . The fiber of  claim 16 , wherein the weight of polymer a) is 20% to 60% of the combined weight of polymer a) and polymer b) and the weight of polymer b is 40% to 80% of the combined weight of polymer a) and polymer b). 
     
     
         19 . The fiber of  claim 12 , wherein the polyhydroxyalkanoate is further blended with polymer c) a poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with a 20% to 50% 4-hydroxybutyrate content. 
     
     
         20 . The fiber of  claim 12 , wherein the polyhydroxyalkanoate is further blended with c) a poly(3-hydroxybutyrate-co-5-hydroxyvalerate) with a 20% to 50% 5-hydroxyvalerate content. 
     
     
         21 . The fiber of  claim 12 , wherein the polyhydroxyalkanoate further blended with c) a poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with a 5% to 50% 3-hydroxyhexanoate content. 
     
     
         22 . The fiber of  claim 19 , wherein the weight of polymer c) is 5% to 95% of the combined polymer weight of polymer a), polymer b) and polymer c). 
     
     
         23 . The fiber of  claim 21 , wherein the weight of polymer c) is 5% to 40% of the combined polymer weight of polymer a), polymer b) and polymer c). 
     
     
         24 . A non-woven web, comprising the fiber of  claim 1 . 
     
     
         25 . A disposable article, comprising the fiber of  claim 1 . 
     
     
         26 . An extruded melt-blown fiber comprising between about 85% and about 95% by weight biologically-produced polyhydroxybutyrate, between about 5% and about 15% acetyl tri-n-butyl citrate, wherein the fiber has a weight-average molecular weight of at least about 200 kg/mol. 
     
     
         27 . An extruded fiber comprising a biologically-produced polyhydroxyalkanoate a plasticizer, and a wet milled nucleating agent wherein the fiber has a weight-average molecular weight of at least about 150 kg/mol. 
     
     
         28 . A fiber comprising a polymer, a plasticizer and a nucleating agent, wherein the nucleating agent is dispersed in the polymer and wherein at least 5% of the cumulative solid volume of the nucleating agent exists as particles with a particle size of 5 microns or less.