Fabric including polyolefin elastic fiber

Abstract

An article comprising a yarn comprising an elastomeric propylene-based polymer composition; said polymer composition comprising at least one elastomeric propylene-based polymer, wherein said yarn has a draft greater than 200%; wherein said article is a fabric or a garment.

1 . An article comprising a yarn comprising an elastomeric propylene-based polymer composition; said polymer composition comprising at least one elastomeric propylene-based polymer, wherein said yarn has a draft greater than 200%; wherein said article is a fabric or a garment. 
     
     
         2 . The article of  claim 1 , wherein said elastomeric propylene-based polymer comprises a diene. 
     
     
         3 . The article of  claim 1 , wherein said elastomeric propylene-based polymer composition comprises a crosslinking agent. 
     
     
         4 . The article of  claim 1 , wherein said elastomeric propylene-based polymer comprises a blend of two or more elastomeric propylene-based polymers. 
     
     
         5 . The article of  claim 1 , wherein said yarn comprises a number of filaments, wherein the number is one to about eighty. 
     
     
         6 . The article of  claim 1 , wherein said yarn comprises a denier of about 10 to about 300. 
     
     
         7 . The article of  claim 3 , wherein said yarn is crosslinked. 
     
     
         8 . The article of  claim 1 , wherein said yarn has an elongation of 200% to about 600%. 
     
     
         9 . A method for preparing a fabric including an elastomeric propylene-based polymer yarn comprising
 (a) providing an elastomeric propylene-based polymer composition;   (b) heating said elastomeric propylene-based polymer composition to a temperature of about 220° C. to about 300° C.;   (c) extruding said composition through a capillary to form a yarn; and   (d) optionally winding said yarn onto a package; and   (e) preparing a fabric including said yarn.   
     
     
         10 . The method of  claim 9 , wherein said winding speed is greater than about 400 m/min. 
     
     
         11 . The method of  claim 9 , wherein said winding speed is greater than about 425 m/min. 
     
     
         12 . The method of  claim 9 , wherein said winding speed is greater than about 500 m/min. 
     
     
         13 . The method of  claim 9 , further comprising:
 (f) crosslinking said yarn.   
     
     
         14 . The method of  claim 13 , wherein the crosslinking is effected by exposing the yarn to an ebeam. 
     
     
         15 . The method of  claim 14 , wherein said yarn is exposed to the ebeam prior to winding on said package. 
     
     
         16 . The method of  claim 13 , wherein said package is exposed to an ebeam as a single package or a plurality of packages in a container. 
     
     
         17 . A method for preparing fabric including an elastomeric propylene-based polymer yarn comprising:
 (a) providing an elastomeric propylene-based polymer composition;   (b) heating said elastomeric propylene-based polymer composition to a temperature of about 220° C. to about 300° C.;   (c) extruding said composition through a capillary to form a yarn;   (d) optionally winding said yarn onto a package;   (e) preparing a warp comprising a plurality of said yarns;   (f) exposing said yarns to an ebeam to crosslink said yarns;   (g) taking up the yarn on a beam; and   (h) warp knitting a fabric.