Aerosol method and apparatus, particulate products, and electronic devices made therefrom

Abstract

Provided is an aerosol method, and accompanying apparatus, for preparing powdered products of a variety of materials involving the use of an ultrasonic aerosol generator ( 106 ) including a plurality of ultrasonic transducers ( 120 ) underlying and ultrasonically energizing a reservoir of liquid feed ( 102 ) which forms droplets of the aerosol. Carrier gas ( 104 ) is delivered to different portions of the reservoir by a plurality of gas delivery ports ( 136 ) delivering gas from a gas delivery system. The aerosol is pyrolyzed to form particles, which are then cooled and collected. The invention also provides powders made by the method and devices made using the powders.

1 . A method of preparing a product comprising particles having a metallic material phase coated with a coating of a metal oxide material phase, the method comprising the steps of:
 generating droplets dispersed in a flowing gas stream, the droplets comprising a liquid and a precursor for at least a component of the metal oxide material phase of the coated particles; and   forming the coated particles, the forming comprising removal of liquid from the droplets at an elevated temperature in a reactor.   
   
   
       2 . The method of  claim 1 , wherein the droplets further comprise a precursor for a component of the metallic material phase. 
   
   
       3 . The method of  claim 1 , wherein the droplets comprise metallic particulates, the particulates comprising a component of the metallic material phase. 
   
   
       4 . The method of  claim 1 , wherein the coating has an average thickness of less than 100 nanometers. 
   
   
       5 . The method of  claim 1 , wherein the coating has an average thickness of less than 50 nanometers. 
   
   
       6 . The method of  claim 1 , wherein the metallic material phase comprises a metal selected from the group consisting of palladium (Pd), silver (Ag), nickel (Ni), copper (Cu), gold (Au), platinum (Pt), molybdenum (Mo), tungsten (W), tantalum (Ta), aluminum (Al) and alloys thereof. 
   
   
       7 . The method of  claim 1 , wherein the metallic material phase comprises silver. 
   
   
       8 . The method of  claim 1 , wherein the metal oxide material phase comprises a metal oxide selected from the group consisting of oxides of zinc, tin, barium, molybdenum, manganese, vanadium, niobium, tantalum, tungsten, iron, silver, chromium, cobalt, nickel, copper, yttrium, iridium, beryllium, silicon, zirconium, aluminum, bismuth, magnesium, thorium and gadolinium. 
   
   
       9 . The method of  claim 1 , wherein the metal oxide material phase comprises a metal oxide selected from the group consisting of silica, alumina, titania, zirconia, yttria, and oxides of copper, bismuth and tin. 
   
   
       10 . The method of  claim 1 , wherein the metal oxide material phase comprises silica. 
   
   
       11 . The method of  claim 1 , wherein the metal oxide material phase comprises a metal oxide selected from the group consisting of borates, titanates, silicates, aluminates, niobates, zirconates and tantalates. 
   
   
       12 . The method of  claim 1 , wherein during the forming, a maximum average stream temperature in the reactor is in a range of from 500° C. to 1500° C. 
   
   
       13 . The method of  claim 1 , wherein the reactor comprises a tubular hot wall furnace. 
   
   
       14 . The method of  claim 1 , wherein the reactor comprises a flame reactor. 
   
   
       15 . The method of  claim 1 , wherein the reactor comprises a plasma reactor. 
   
   
       16 . The method of  claim 1 , wherein the coated particles have a weight average particle size of from about 0.1 μm to about 4 μm. 
   
   
       17 . The method of  claim 1 , wherein the generating comprises producing the droplets from a spray nozzle atomizer. 
   
   
       18 . The method of  claim 1 , wherein the generating comprises sweeping away with carrier gas said droplets as said droplets are released from a reservoir of an ultrasonically energized flowable medium, said flowable medium comprising the liquid and the precursors and said flowable medium being ultrasonically energized by a plurality of ultrasonic transducers underlying said reservoir. 
   
   
       19 . A method of preparing a product comprising particles having a metallic material phase coated with a coating of a metal oxide material phase, where the metallic material phase comprises silver, the method comprising the steps of:
 generating droplets dispersed in a flowing gas stream, the droplets comprising a liquid and a precursor for at least a component of the metal oxide material phase of the coated particles; and   forming the coated particles, the forming comprising removal of liquid from the droplets at an elevated temperature in a reactor.   
   
   
       20 . The method of  claim 19 , wherein the metal oxide material phase comprises silica.