Light phosphor with zeolitic structure

Abstract

The present invention is related to a phosphor that can be excited by UV light between 375 to 400 nm to emit white light, which is intrinsically produced by emitting blue light with yellow light simultaneously. This compound is synthesized from organic amine, metal oxide and phosphate under hydrothermal conditions, and gives rise to a zeolitic structure with the chemical formula of (A) 5-x/2 [Zn 9-x Ga x O(HPO 4 )(PO 4 ) 8 ].yH 2 O (0<x<9, 0<y<15). On the other hand, when synthesized by different solvents, it is possible to obtain a phosphor of the same chemical formula and structure, but it can emit yellow light when excited by UV light or blue light emitted by LED between 300 to 500 nm.

1 - 12 . (canceled) 
   
   
       13 . A method for preparing a phosphor having a chemical formula as follows:
   (A) 5-x/2 [M 9-x Ga x O(HPO 4 )(PO 4 ) 8 ].yH 2 O   wherein 0<x<9; 0<y<15, M is a transition metal, and A is a cation of Group 1A metal or a protonated organic amine, said method comprising the following steps:   preparing a mixed solution comprising a gallium source, a source of M, phosphate, a template, and water, and optionally an alcohol; and   heating the mixed solution to carry out a hydrothermal reaction, wherein the gallium source comprises a gallium metal, a gallium salt, or a gallium oxides, and the M source comprises a M metal, a M metal salt, or a M metal oxide.   
   
   
       14 . The method of  claim 13 , wherein the template comprises an organic amine. 
   
   
       15 . The method of  claim 14 , wherein the organic amine is 4,4′-trimethylenedipyridine. 
   
   
       16 . The methods of  claim 13 , wherein M is a transition metal of Group 2B. 
   
   
       17 . The method of  claim 15 , wherein M is Zn. 
   
   
       18 . The method of  claim 16 , wherein the alcohol is ethylene glycol or n-butanol. 
   
   
       19 . The method of  claim 17 , wherein x is 6; y is 5. 
   
   
       20 . The method of  claim 19 , wherein the mole ratio of 4,4′-trimethylenedipyridine:Zn:Ga:H 3 PO 4  in the mixed solution equals to 6.4:1:1:6. 
   
   
       21 . The method of  claim 20 , wherein the mixed solution does not comprise the alcohol. 
   
   
       22 . The method of  claim 20 , wherein the mixed solution comprises the alcohol. 
   
   
       23 . The method of  claim 21 , wherein when the phosphor is excited by a light from UV light to blue light with a wavelength between 270 to 500 nm, it emits yellow light with a wavelength between 520 to 620 nm. 
   
   
       24 . The method of  claim 22 , wherein when the phosphor is excited by a light source with a wavelength between 270 to 420 nm, it emits blue light with a wavelength between 400 to 500 nm; when it is excited by a light source with a wavelength between 280 to 500 nm, it emits yellow light with a wavelength between 520-650; when it is excited by a light source with a wavelength between 280 to 420, it emits white light that is produced by mixing blue light and yellow light. 
   
   
       25 . The method of  claim 19  further comprising contacting the resulting phosphor from the hydrothermal reaction with a solution containing cations of Group 1A metal, so that the protonated 4,4′-trimethylenedipyridine and the cations of Group 1A metal are cation exchanged. 
   
   
       26 . The method of  claim 16 , wherein the hydrothermal reaction is carried out at 160 to 180° C. for a period of 1 to 10 days. 
   
   
       27 . The method of  claim 26 , wherein the hydrothermal reaction is carried out for a period of 3 to 7 days. 
   
   
       28 . The method of  claim 13 , wherein the hydrothermal reaction is carried out in the mixed solution having a pH value of 3.5 to 6.5. 
   
   
       29 . The method of  claim 28 , wherein the pH value is 5.0. 
   
   
       30 . The method of  claim 13 , wherein the mixed solution further comprises a diacid. 
   
   
       31 . The method of  claim 30 , wherein the diacid is oxalic acid.