Perfluorinated polymers

Abstract

Amorphous perfluorinated homopolymers and copolymers of perfluorodioxoles of formula (IA): wherein R′ F is equal to R F or OR F wherein R F is a linear or branched perfluoroalkyl radical having 1-5 carbon atoms; X 1 and X 2 , equal to or different from each other, are F, CF 3 ; said polymers having a dioxole content ≧95% by moles, having the following property combination: Tg, measured according to the ASTM 3418 (DSC) method, from 180° C. to 195° C.; intrinsic viscosity, measured at the temperature of 30° C. in perfluoroheptane (Galden® D80) according to the ASTM D 2857-87 method, from 13 cc/g to 100 cc/g.

1 . Amorphous perfluorinated homopolymers and copolymers of perfluorodioxoles of formula (IA):  
     
       
         
         
             
             
         
       
     
     wherein R′ F  is equal to F or R F  or OR F  wherein R F  is a linear or branched perfluoroalkyl radical having 1-5 carbon atoms; X 1  and X 2 , equal to or different from each other, are F, CF 3 ;  
     having a dioxole content ≧95% by moles, having the following combination of properties: 
 Tg, measured according to the ASTM 3418 (DSC) method, from 180° C. to 195° C.;  
 intrinsic viscosity, measured at the temperature of 30° C. in perfluoroheptane according to the ASTM D 2857-87 method, from 13 cc/g to 100 cc/g.  
 
   
   
       2 . Amorphous perfluorinated homopolymer and copolymers according to  claim 1 , wherein in formula R′ F =OCF 3 ; X 1 =X 2 =F.  
   
   
       3 . Amorphous perfluorinated homopolymer and copolymers according to  claim 1 , selected among the homopolymers of the perfluorodioxole of formula wherein R′ F =OCF 3 ; X 1 =X 2 =F.  
   
   
       4 . Amorphous perfluorinated homopolymers and copolymers according to  claim 1 , wherein the homopolymers and copolymers further comprise comonomers selected from one or more of the following: 
 C 2 -C 8  perfluoroolefins, selected between tetrafluoroethylene (TFE), hexafluoropropene (HFP);    perfluoroalkylvinylethers CF 2 =CFOR f , wherein R f  is a C 1 -C 6  perfluoroalkyl;    perfluoro-oxyalkylvinylethers CF 2 =CFOX, wherein X is selected from the group consisting of: C 1 -C 12  alkyl, C 1 -C 12  oxyalkyl, and C 1 -C 12  (per)fluoro-oxyalkyl having one or more ether groups;    perfluorodioxoles, wherein in formula (IA) R′ F  is F; X 1  and X 2 , equal to or different from each other, are selected between F or R F ;    perfluorovinylethers of general formula CFX AI =CX AI OCF 2 OR AI (A-I) wherein: 
 R AI  is selected from the group consisting of: a C 2 -C 6  linear, branched perfluoroalkyl group, a C 5 -C 6  cyclic perfluoro oxyalkyl group, and a C 2 -C 6  linear or branched perfluoro oxyalkyl group containing from one to three oxygen atoms;  
 R AI  can optionally contain from 1 to 2 atoms, equal or different, selected from the following: Cl, Br, I;  
 X AI =F.  
   
   
   
       5 - 8 . (canceled)  
   
   
       9 . Amorphous perfluorinated homopolymers and copolymers of  claim 1 , wherein the ionic end groups are completely absent when determined by the analytical method described hereunder, said polymers obtainable by treating with elemental fluorine, optionally in admixture with inert gases, in an inert solvent at fluorination, in the presence of ultraviolet radiations having a wave length from 200 to 500 nm, operating at temperatures lower than 100° C. for reaction times from 10 h to 60 h.  
     
       
         
           
             
               '' 
               ⁢ 
               Difference 
               ⁢ 
               
                   
               
               ⁢ 
               
                 spectrum 
                 ⁢ 
                 '' 
               
             
             
               [ 
               
                 pellet 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 weight 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 
                   
                     ( 
                     g 
                     ) 
                   
                   / 
                   pellet 
                 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 area 
                 ⁢ 
                 
                     
                 
                 ⁢ 
                 
                   ( 
                   
                     cm 
                     2 
                   
                   ) 
                 
               
               ] 
             
           
         
       
     
   
   
       10 . Amorphous perfluorinated homopolymers and copolymers according to  claim 9 , wherein the unstable ionic end groups are COF, COOH, their esters, salts or amidic derivatives.  
   
   
       11 . Amorphous perfluorinated homopolymers and copolymers according to  claim 9 , wherein the radiation used in the fluorination process has a wave length ranging from 200 to 500 nm and the reaction temperature ranges from 0° C. to +100° C.  
   
   
       12 . Amorphous perfluorinated homopolymers and copolymers according to  claim 9 , wherein in the fluorination process the polymer concentration in the solvent is between 1 and 10% by weight.  
   
   
       13 . Amorphous perfluorinated homopolymers and copolymers according to  claim 9 , wherein a perfluorinated solvent is used, selected from perfluoroalkanes, perfluoropolyethers.  
   
   
       14 - 20 . (canceled)  
   
   
       21 . Amorphous perfluorinated homopolymers and copolymers of  claim 1 , wherein R′ F =OCF 3 .  
   
   
       22 . Amorphous perfluorinated homopolymers and copolymers of  claim 1 , wherein Tg is 190° C. to 192° C.  
   
   
       23 . Amorphous perfluorinated homopolymers and copolymers of  claim 4 , wherein the comonomers are perfluoroalkylvinylethers CF 2 =CFOR f , wherein R f  is CF 3 , C 2 F 5 , or C 3 F 7 .  
   
   
       24 . Amorphous perfluorinated homopolymers and copolymers of  claim 4 , wherein the comonomers are perfluoro-oxyalkylvinylethers CF 2 =CFOX, wherein X is perfluoro-2-propoxy-propyl.  
   
   
       25 . Amorphous perfluorinated homopolymers and copolymers of  claim 4 , wherein the comonomers are perfluorodioxoles, wherein R′ F  is F and X 1 =X 2 =CF 3 .  
   
   
       26 . Amorphous perfluorinated homopolymers and copolymers of  claim 4 , wherein the comonomers are perfluorovinylethers CF 2 =CFOCF 2 OCF 2 CF 3  or (MOVE II) CF 2 =CFOCF 2 OCF 2 CF 2 OCF 3 .