Glass substrate for information recording medium and magnetic information recording medium to which the glass substrate is applied

Abstract

Disclosed are a glass substrate for an information recording medium, having excellent scratch resistance and a light weight and having high fracture toughness, the glass substrate having a fragility index value, measured in water, of 12 μm −1/2 or less or having a fragility index value, measured in an atmosphere having a dew point of −5° C. or lower, of 7 μm −1/2 or less, or the glass substrate comprising, by mol %, 40 to 75% of SiO 2 , 2 to 45% of B 2 O 3 and/or Al 2 O 3 and 0 to 40% of R′ 2 O in which R′ is at least one member selected from the group consisting of Li, Na and K), wherein the total content of SiO 2 , B 2 O 3 , Al 2 O 3 and R′ 2 O is at least 90 mol %, and a magnetic information recording medium comprising a magnetic recording layer formed on the glass substrate.

1 . A glass substrate for an information recording medium, having a fragility index value, measured in water, of 12 μm −1/2  or less.  
   
   
       2 . A glass substrate for an information recording medium, having a fragility index value, measured in an atmosphere having a dew point of −5° C. or lower, of 7 μm −1/2  or less.  
   
   
       3 . A glass substrate for an information recording medium, having a fragility index value, measured in water, of 12 μm −1/2  or less and having a fragility index value, measured in an atmosphere having a dew point of −5° C. or lower, of 7 μm −1/2  or less.  
   
   
       4 . The glass substrate for an information recording medium as recited in  claim 1 , comprising, by mol %, greater than 65%, as a total, of SiO 2  and at least one of B 2 O 3  and Al 2 O 3 , 0 to 20% of RO in which R is at least one member selected from the group consisting of Ma, Ca, Zn, Sr and Ba, 0 to 28% of R′ 2 O in which R′ is at least one member selected from the group consisting of Li, Na and K, 0 to 10% of TiO 2  and 0 to 10% of ZrO 2 , the total content of said components being at least 95 mol %.  
   
   
       5 . A glass substrate for an information recording medium, comprising, by mol %, 40 to 75% of SiO 2 , 2 to 45% of B 2 O 3  and/or Al 2 O 3  and 0 to 40% of R′ 2 O in which R′ is at least one member selected from the group consisting of Li, Na and K), wherein the total content of SiO 2 , B 2 O 3 , Al 2 O 3  and R′ 2 O is at least 90 mol %.  
   
   
       6 . The glass substrate for an information recording medium as recited in  claim 5 , having a fragility index value, measured in water, of 12 μm −1/2  or less.  
   
   
       7 . The glass substrate for an information recording medium as recited in  claim 5 , having a fragility index value, measured in an atmosphere having a dew point of −5° C. or lower, of 7 μm −1/2  or less.  
   
   
       8 . The glass substrate for an information recording medium as recited in  claim 1 , having a Young's modulus of at least 70 GPa.  
   
   
       9 . The glass substrate for an information recording medium as recited in  claim 1 , having a modulus of rigidity of at least 20 GPa.  
   
   
       10 . The glass substrate for an information recording medium as recited in  claim 1 , which is made of a glass having a region wherein the glass has a viscosity of at least 1 Pa·s, in a range of temperatures equivalent to, and higher than, a liquidus temperature of the glass.  
   
   
       11 . The glass substrate for an information recording medium as recited in  claim 1 , which is made of a glass having a thermal expansion coefficient of 60×10 −7 /° C. or greater at a temperature of from 100° C. to 300° C.  
   
   
       12 . The glass substrate for an information recording medium as recited in  claim 1 , which has no chemically strengthened layer.  
   
   
       13 . The glass substrate for an information recording medium as recited in  claim 1 , which has a chemically strengthened layer.  
   
   
       14 . A magnetic information recording medium comprising a magnetic recording layer formed on the glass substrate for an information recording medium recited in  claim 1.