Multilayer spunlaced nonwoven fire blocking composite

Abstract

This invention relates to a mulilayer spunlaced nonwoven composite useful as a fire blocking component for an article, an article such as furniture or a mattress comprising the nonwoven composite, and processes for making the nonwoven composite and fire blocking an article with the nonwoven composite. The multilayer nonwoven composite comprises a first layer comprising 75 to 25 weight percent regenerated cellulosic fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute and 25 to 75 weight percent heat-resistant fiber, said first layer having a basis weight of from 1 to 5 ounces per square yard (34 to 170 grams per square meter); and a second layer comprising up to 75 weight percent of a regenerated cellulosic fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute, and 25 to 100 weight percent of a modacrylic fiber, said second layer having a basis weight of from 1 to 5 ounces per square yard (34 to 170 grams per square meter), the nonwoven composite having a total basis weight of from 2 to 7 ounces per square yard (68 to 237 grams per square meter).

1 - 11 . (canceled)  
   
   
       12 . A method making a nonwoven composite useful in fire blocking, comprising the steps of 
 a) combining a first layer and a second layer of staple fibers, the first layer of staple fibers comprising 75 to 25 weight percent regenerated cellulosic fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute and 25 to 75 weight percent heat-resistant fiber, and    the second layer of staple fibers comprising up to 75 weight percent regenerated cellulosic fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute and 25 to 100 weight percent modacrylic fiber; and    b) hydrolacing the first and second layers together to consolidate the layers and form a unitary nonwoven composite.    
   
   
       13 . The method of making a nonwoven composite of  claim 12 , wherein the first layer of staple fibers is superposed over the second layer of staple fibers prior to hydrolacing.  
   
   
       14 . The method of making a nonwoven composite of  claim 12 , wherein the first and second layers are consolidated by hydrolacing such that the total hand measurement of the nonwoven composite is less than 500 grams force.  
   
   
       15 . The method of making a nonwoven composite of  claim 12 , wherein the first layer of staple fibers has a basis weight of 1 to 5 ounces per square yard (34 to 170 grams per square meter).  
   
   
       16 . The method of making a nonwoven composite of  claim 12 , wherein the second layer of staple fibers has a basis weight of 1 to 5 ounces per square yard (34 to 170 grams per square meter).  
   
   
       17 . A method of fire blocking an article, comprising the steps of 
 a) combining a layer of nonwoven fire blocking composite, a fabric ticking or upholstery layer, and optionally a cushioning layer,    b) sewing the layers together to form a fire blocked quilt or upholstery fabric, and    c) incorporating the fire blocked quilt or upholstery fabric into the article, the nonwoven fire blocking composite comprising a first layer of staple fibers comprising 75 to 25 weight percent regenerated cellulosic fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute and 25 to 75 weight percent heat-resistant fiber, 
 said first layer having a basis weight of from 1 to 5 ounces per square yard (34 to 170 grams per square meter); and  
 a second layer of staple fibers comprising up to 75 weight percent regenerated cellulosic fiber that retains at least 10 percent of its fiber weight when heated in air to 700° C. at a rate of 20 degrees C. per minute, and 25 to 100 weight percent modacrylic fiber,  
 said second layer having a basis weight of from 1 to 5 ounces per square yard (34 to 170 grams per square meter); the nonwoven composite having a total basis weight of from 2 to 7 ounces per square yard (68 to 237 grams per square meter).  
   
   
   
       18 . The method of fire blocking an article of  claim 17 , wherein the heat-resistant fiber is a para-aramid fiber.  
   
   
       19 . The method of fire blocking an article of  claim 17 , wherein first layer comprises 55 to 45 weight percent regenerated cellulosic fiber containing silicic acid and 45 to 55 weight percent poly(paraphenylene terephthalamide) fiber, and second layer comprises 25 to 40 weight percent regenerated cellulosic fiber containing silicic acid and 75 to 60 weight percent modacrylic fiber.  
   
   
       20 . The method of fire blocking an article of  claim 17 , wherein the regenerated cellulosic fiber contains silicic acid.  
   
   
       21 - 24 . (canceled)