Curable compositions and rapid prototyping process using the same

Abstract

A radiation curable composition comprising 10-90 wt % of a cationically polymerizable compound, 0.1-10 wt % of a cationic photoinitiator, 1-40 wt % of a radically polymerizable compound, 0.1-10 wt % of a radical photoinitiator and 5-70 wt % of a filler having a mean average particle size of between 3 and 500 nanometer.

1 . A radiation curable composition comprising 
 a 10-90 wt % of a cationically polymerizable compound    b 0.1-10 wt % of a cationic photoinitiator    c 1-40 wt % of a radically polymerizable compound    d 0.1-10 wt % of a radical photoinitiator and    e 5-70 wt % of a filler having a mean average particle size of between 3 and 500 nanometer.    
     
     
         2 . The radiation curable composition according to  claim 1 , wherein the mean average particle size of the filler is below 200 nanometer.  
     
     
         3 . The composition according to  claim 1 , wherein the mean average particle size of the filler is below 50 nanometer.  
     
     
         4 . The composition according to  claim 1 , wherein the amount of filler ranges between 5 and 50 wt %  
     
     
         5 . The composition according to  claim 1 , wherein the amount of filler ranges between 20 and 45 wt %.  
     
     
         6 . The composition according to  claim 1 , wherein the cationically polymerizable compound contains epoxy-functional components and/or oxetane-functional components.  
     
     
         7 . The composition according to  claim 1 , wherein the composition comprises one or more mono or poly glycidylethers of aliphatic alcohols, aliphatic polyols, polyesterpolyols or polyetherpolyols.  
     
     
         8 . The composition according to  claim 1 , wherein the composition contains between 5 and 20 wt % of mono or poly glycidyl ethers of an aliphatic alcohol, aliphatic polyols, polyesterpolyol or polyetherpolyol.  
     
     
         9 . The composition according to  claim 1 , wherein the radically polymerizable compound contains one or more (meth)acrylate groups.  
     
     
         10 . The composition according to  claim 9 , wherein radically polymerizable compound comprises one or more components having at least 3 (meth)acrylate groups.  
     
     
         11 . The composition according to  claim 1 , wherein a component is present having a polyether backbone.  
     
     
         12 . The composition according to  claim 11 , wherein the component having a polyether backbone is selected from the group consisting of polytetramethylenediol, glycidylethers of polytetramethylenediol, acrylates of polytetramethylenediol or polytetramethylenediol containing one or more polycarbonate groups.  
     
     
         13 . The composition according to  claim 11 , wherein the compound having a polyether backbone is present in an amount ranging from 5 to 20 wt %.  
     
     
         14 . The composition according to  claim 1 , wherein the composition comprises a dispersant.  
     
     
         15 . The composition according to  claim 14 , wherein the dispersant is a compound selected from organosiloxanes, functionalised organosiloxanes, alkyl-substituted pyrrolidones, polyoxyalkylene ethers, ethyleneoxide propylenenoxide block copolymers.  
     
     
         16 . The composition according to  claim 14 , wherein the amount of dispersant is between 0.1 and 2 wt %.  
     
     
         17 . The composition according to  claim 1 , wherein after full cure, the composition has an elongation at break of at least 1.0%,  
     
     
         18 . The composition according to  claim 1 , wherein after full cure, the composition has a tensile strength of at least 40 MPa  
     
     
         19 . The composition according to  claim 1 , wherein after full cure, the composition has a tensile strength of at least 50 MPa.  
     
     
         20 . The composition according to  claim 1 , wherein after full cure, the article has a Young's modulus of at least 2500 MPa  
     
     
         21 . The composition according to  claim 1 , wherein after full cure, the article has a Young's modulus of at least 3000 MPa  
     
     
         22 . A rapid prototyping process comprising the steps: 
 (1) coating a layer of a composition onto a surface;    (2) exposing said layer imagewise to actinic radiation to form an imaged cross-section;    (3) coating a further layer of the composition onto said imaged cross-section;    (4) exposing said further layer imagewise to actinic radiation to form an additional imaged cross-section;    (5) repeating steps (3) and (4) a sufficient number of times in order to build up a three-dimensional article;    (6) optionally, post-curing the three-dimensional article,    wherein a composition is used as defined in  claim 1 .    
     
     
         23 . A three dimensional article comprising: 
 a composition comprising. 
 a cationically polymerizable compound;  
 a radically polymerizable compound; and  
 5-70 wt % of a filler having a mean average particle size of between 3 and 500 nanometer;  
   said article for after full cure, having an elongation at break of at least 1.0%, and a tensile strength of at least 40 MPa.    
     
     
         24 . The article according to  claim 23 , wherein the article has a tensile strength of at least 50 MPa.  
     
     
         25 . The article according to  claim 23 , wherein the article has a Young's modulus of at least 3000 MPa.  
     
     
         26 . The article according to  claim 23 , wherein the article has a Young's modulus of at least 3500 MPa.