Abstract

An aqueous coating composition having improved adhesion to friable surfaces including an emulsion polymer of certain compositions and certain acid numbers having a glass transition temperature of −20° C. to 100° C. and an average particle diameter less than 120 nanometers, and certain water-soluble ethoxylates is provided. In addition, a method for improving adhesion to friable surfaces by using the aqueous coating compositions of the invention is provided.

1 - 3 . (canceled)  
     
     
         4  An aqueous coating composition having improved adhesion to friable surfaces comprising: 
 (a) an emulsion polymer having a glass transition temperature of -20° C. to 100° C. and an average particle diameter less than 120 nanometers, said emulsion polymer consisting essentially of: 
 (i) 8-99.5%, by weight based on said emulsion polymer weight, of at least one copolymerized ethylenically unsaturated first nonionic monomer, each of said first nonionic monomer(s) having a water solubility of at least 8% by weight based on the weight of water;  
 (ii) 0-91.5%, by weight based on said emulsion polymer weight, of at least one copolymerized ethylenically unsaturated second nonionic monomer, each of said second nonionic monomer(s) having a water solubility of less than 8% by weight based on the weight of water; and  
 (iii) at least 0.5%, by weight based on said emulsion polymer weight, of at least one copolymerized acid monomer, such that the acid number of said emulsion polymer is 4 to 100;  
 wherein said emulsion polymer is made without the use of chain transfer agent; and  
   (b) 0.25-10%, by dry weight based on the dry weight of said emulsion polymer, nonionic surfactant selected from the group consisting of water-soluble alkyl phenol ethoxylates, alkyl alcohol ethoxylates, and mixtures thereof.    
     
     
         5 . The coating composition of  claim 4  wherein the average particle diameter of said emulsion polymer is less than 80 nanometers.  
     
     
         6 - 10 . (canceled)