Addition of organic initiators during the pressure drop In vinyl chloride monomer polymerization reactions

Abstract

The invention pertains to a process to polymerize one or more monomers wherein one or more initiators and optionally one or more surfactants are added to a polymerization mixture when the pressure in the polymerization reactor is dropping. This process allows a shorter polymerization time due to a higher pressure drop rate at the end of the polymerization reaction. Moreover, the cooling capacity of the polymerization reactor is used more efficiently.

1 . Process wherein two or more initiators are used to polymerize a mixture containing one or more monomers of which one is vinyl chloride monomer, wherein a conventional initiating system is added to the polymerization mixture in the first part of the polymerization reaction and one or more additional initiators are added to the polymerization mixture at the reaction temperature when the pressure in the polymerization reactor is dropping due to the depletion of the vinyl chloride monomer and said additional initiators have a half-life of less than 1 hour at the polymerization temperature, with the proviso that the polymer formed is not subject to radio frequency dielectric heating in the presence of additional organic initiator.  
     
     
         2 . A process according to  claim 1  wherein the initiator added after the start of the pressure drop and/or during the pressure drop has a half-life of from 0.0001 hour to 1 hour at the polymerization temperature.  
     
     
         3 . A process according to  claim 2  wherein the additional organic initiator added after and/or during the pressure drop has a half-life of from 0.0001 hour to 0.05 hour at the polymerization temperature.  
     
     
         4 . A process according to any one of claims  1 - 3  wherein at least part of the initiators is added intermittently and/or continuously after the start of the pressure drop and/or during the pressure drop.  
     
     
         5 . A process according to any one of claims  1 - 4  wherein a surfactant is also added when the pressure in the polymerization reactor is dropping due to the depletion of the vinyl chloride monomer to reduce the formation of foam.