Passivating of tin, zinc and steel surfaces

Abstract

A method for coating zinc, zinc plated, or steel articles with a hydroxy benzoic acid protective coating by coating a cleaned zinc, zinc plated, or steel with a hydoxy benzoic acid composition having a pH of about 2.0 to 5.0; and coating cleaned tin surfaced articles with a composition having a PH of 2.0 to 12.0, and the composition having as its essential ingredients proteins, amino acids, amino acid-protein compounds and amine alcohols; and the articles produced thereby along with the coated articles having an appropriate paint thereon.

1 . A passified zinc, zinc plated, or steel article having coated thereon a hydroxy benzoic acid composition wherein the hydroxy benzoic acid composition will allow the article to be painted with an appropriate paint.  
     
     
         2 . The passified zinc, zinc plated, or steel article of  claim 1 , wherein the said hydroxy benzoic acid is selected from the group consisting of di- and tri-hydroxy benzoic acids and mixtures thereof.  
     
     
         3 . The passified zinc, zinc plated, or steel article of  claim 8 , wherein the dihydroxy benzoic acid is resorcylic acid and the trihydroxy benzoic acid is selected from 2,3,4-, 2,4,6-, and 3,4,5-trihydroxy benzoic acid and mixtures thereof.  
     
     
         4 . The passified zinc, zinc plated, or steel article of  claim 3 , wherein the article has a layer of an appropriate paint over the hydroxy benzoic acid composition to provide a paint protected zinc, zinc plated, or steel article that passes the ASTM-D3359 paint adhesion test.  
     
     
         5 . A method of preparing the zinc, zinc plated, or steel article of  claim 1  comprising coating a cleaned zinc, zinc plated, or steel article with a composition having a PH of 2.0 to about 5.0, and said composition having as its essential compound a hydroxy benzoic acid.  
     
     
         6 . The method of  claim 5 , wherein said hydroxy benzoic acid is selected from the group consisting of di- and tri- hydroxy benzoic acids and mixtures thereof.  
     
     
         7 . The method of  claim 6 , wherein the pH of the composition is about 2.5 to 4.5.  
     
     
         8 . The method of  claim 6 , wherein the dihydroxy benzoic acid is selected from the group consisting of resorcylic acid, 2,3,4-, 2,4,6-, and 3,4,5-trihydroxy benzoic acid, and mixtures thereof.  
     
     
         9 . The method of  claim 8 , wherein the pH of the composition is about 2.5 to 4.5.  
     
     
         10 . The method of  claim 8 , comprising the further steps of drying the benzoic acid coated zinc, zinc plated or steel article, and painting the dried article to provide a paint protected zinc, zinc plated steel article that will pass the ASTM-D3359 paint adhesion test.  
     
     
         11 . A method of coating an article having a tin surface with a protective coating comprising coating a cleaned tin surface article with a composition having a PH of 2.0 to 12.0, and said composition having as its essential ingredients proteins, amino acids, amino acid-protein compounds and amine alcohols.  
     
     
         12 . The method of  claim 11  wherein the pH is 2.5 to 11 and the coating is by electrolysis for 5 seconds or less and at a current density of about 10-25 amps per sq. ft.  
     
     
         13 . The method of  claim 12  wherein said composition contains proteins.  
     
     
         14 . The method of  claim 13  wherein said proteins are selected from the group consisting of casein, gelatin, dried egg white, and mixtures thereof.  
     
     
         15 . The method of  claim 11 , comprising the further steps of drying the coated article, and painting the dried article to provide a paint protected tin surface article that will pass the ASTM-D3359 paint adhesion test.  
     
     
         16 . The method of  claim 15  wherein the pH is 2.5 to 11 and the coating is by electrolysis for 5 seconds or less and at a current density of about 10-25 amps per sq. ft.  
     
     
         17 . The method of  claim 16  wherein said composition contains proteins.  
     
     
         18 . The method of  claim 17  wherein said proteins are selected from the group consisting of casein, gelatin, dried egg white, and mixtures thereof.