Precision press-molding preform, process for the production thereof, optical element and process for the production of the optical element

Abstract

A precision press-molding preform for producing an optical element for use in an imaging device using a CCD type or MOS type solid image-sensing device, which is formed of a glass composition containing, by mol %, 25 to 45% of P 2 05, 0.5 to 10% of CuO, 0 to 10% of B 2 0 3 , 0 to 10% of Al 2 0 3 , 2 to 30% of Li 2 O, 0 to 25% of Na 2 O, 0 to 15% of K 2 O, the total content of Li 2 O, Na 2 O and K 2 O being 3 to 40%, 3 to 45% of BaO, 0 to 30% of ZnO, 0 to 20% of MgO, 0 to 20% of CaO, 0 to 20% of SrO, 0 to 10% of Bi 2 O 3 , 0 to 5% of La 2 O 3 , 0 to 5% of Gd 2 O 3 and 0 to 5% of Y 2 O 3 , the total content of these components being at least 98%, and a precision press-molding preform, which is formed of a phosphate glass containing CuO, an alkali metal oxide, BaO and ZnO and having a BaO content/ZnO content molar ratio (BaO/ZnO) of greater than 1.

1 . A precision press-molding preform, which is formed of a glass composition comprising, by mol %, 25 to 45% of P 2 O 5 , 0.5 to 10% of CuO, 0 to 10% of B 2 O 3 , 0 to 10% of Al 2 O 3 , 2 to 30% of Li 2 O, 0 to 25% of Na 2 O, 0 to 15% of K 2 O, the total content of Li 2 O, Na 2 O and K 2 O being 3 to 40%, 3 to 45% of BaO, 0 to 30% of ZnO, 0 to 20% of MgO, 0 to 20% of CaO, 0 to 20% of SrO, 0 to 10% of Bi 2 O 3 , 0 to 5% of La 2 O3, 0 to 5% of Gd 2 O 3  and 0 to 5% of Y 2 O 3 , the total content of these components being at least 98%.  
     
     
         2 . A precision press-molding preform as recited in  claim 1 , wherein the glass composition has a BaO content/ZnO content molar ratio (BaO/ZnO) of greater than 1.  
     
     
         3 . A precision press-molding preform, which is formed of a phosphate glass containing CuO, an alkali metal oxide, BaO and ZnO and having a BaO content/ZnO content molar ratio (BaO/ZnO) of greater than 1.  
     
     
         4 . A precision press-molding preform as recited in  claim 3 , wherein the phosphate glass contains, by mol %, 25 to 45% of P 2 O 5 , 0.5 to 10% of cuO, 0 to 10% of B 2 O 3 , 0 to 10% of Al 2 O 3 , 3 to 40% of a total of Li 2 O, Na 2 O and K 2 O, 3 to 45% of BaO and 0 to 30% of ZnO.  
     
     
         5 . A precision press-molding preform as recited in  claim 1  or  3 , wherein the glass, when it has a thickness of 1 mm, has, as transmittance characteristics, an external transmittance of 80 to 90% at a wavelength of 400 nm, an external transmittance of 0.1 to 18% at a wavelength of 700 nm, an external transmittance of 1 to 30% at a wavelength of 1,200 nm and a maximum external transmittance at a wavelength of 400 to 600 nm.  
     
     
         6 . A process for the production of a precision press-molding preform, which comprises separating a molten glass gob having a predetermined mass from a molten glass and shaping the molten glass gob into the precision press-molding preform recited in  claim 1  or  3 .  
     
     
         7 . An optical element which is a precision press-molded product from the precision press-molding preform recited  claim 1  or  3 .  
     
     
         8 . An optical element which is a precision press-molded product from that precision press-molding preform which is produced by the process recited in  claim 6 .  
     
     
         9 . An optical element which is a precision press-molded product and is formed of a glass composition comprising, by mol %, 25 to 45% of P 2 O 5 , 0.5 to 10% of CuO, 0 to 10% of B 2 O 3 , 0 to 10% of Al 2 O 3 , 2 to 30% of Li 2 O, 0 to 25% of Na 2 O, 0 to 15% of K 2 O, the total content of Li 2 O, Na 2 O and K 2 O being 3 to 40%, 3 to 45% of BaO, 0 to 30% of ZnO, 0 to 20% of MgO, 0 to 20% of CaO, 0 to 20% of SrO, 0 to 10% of Bi 2 O 3 , 0 to 5% of La 2 O 3 , 0 to 5% of Gd 2 O 3  and 0 to 5% of Y 2 O 3 , the total content of these components being at least 98%.  
     
     
         10 . An optical element which is a precision press-molded product and is formed of a phosphate glass containing Cuo, an alkali metal oxide, BaO and ZnO and having a BaO content/ZnO content molar ratio (BaO/ZnO) of greater than 1.  
     
     
         11 . An optical element as recited in  claim 7 , which is one of an aspherical lens, a spherical lens, a lens array, an optical low-pass filter and a diffraction grating, and has a near infrared absorbing function.  
     
     
         12 . A process for the production of an optical element, which comprises heating the precision press-molding preform recited in  claim 1  or  3  and precision press-molding the preform by means of a press mold.  
     
     
         13 . A process for the production of an optical element, which comprises heating that precision press-molding preform produced by the process recited in  claim 6  and precision press-molding the preform by means of a press mold.  
     
     
         14 . A process for the production of an optical element as recited in  claim 12 , wherein the precision press-molding preform is introduced into the press mold, and the preform and the press mold are heated together for the precision press-molding.  
     
     
         15 . A process for the production of an optical element as recited in  claim 12 , wherein the precision press-molding preform is pre-heated and then introduced into the press mold for precision press-molding.