Process for preparing closed-cell water-blown rigid polyurethane foams having improved mechanical properties

Abstract

The present invention is directed to a process for preparing water-blown rigid polyurethane foams having at least an 80% closed-cell content which involves reacting a) at least one polyol mixture which is composed of (i) at least one polymer polyol; (ii) at least one polyol having a hydroxyl value within the range of from about 200 to about 800; and (iii) optionally, at least one polyol having a hydroxyl value within the range of from about 25 to about 115; with b) at least one polymeric isocyanate and/or a prepolymer thereof; in the presence of c) optionally, at least one catalyst; d) water; and e) optionally, at least one additive or auxiliary agent. The present invention is also directed to the closed-cell water blown rigid polyurethane foams produced by the process of the present invention. The invention is further directed to a polyurethane-foam forming mixture which is used to produce the water-blown rigid polyurethane foams of the present invention. Foams produced according to the present invention have reduced friability and acceptable adhesion to substrates as well as acceptable compressive strength.

1 - 12 . (Cancelled).  
     
     
         13 . A polyurethane-foam forming mixture comprising: 
 (a) at least one polyol mixture comprising: 
 (i) at least one polymer polyol;  
 (ii) at least one polyol having a hydroxyl value within the range of from about 200 to about 800; and  
 (iii) optionally, at least one polyol having a hydroxyl value within the range of from about 25 to about 1 15;  
   (b) at least one polymeric isocyanate and/or a prepolymer thereof;    (c) optionally, at least one catalyst;    (d) water; and    (e) optionally, at least one additive or auxiliary agent    wherein foam made from the mixture has a perpendicular compressive strength within the range of from about 35 to about 105 lbs/in 2  and a tensile adhesion greater than 105 lbs/in 2 .    
     
     
         14 . The mixture of  claim 13  in which polymer polyol (i) is comprised of at least one solid which is the reaction product of a mixture of 2,4- and 2,6-toluene diisocyanate and hydrazine polymerized in situ in a polyether polyol.  
     
     
         15 . The mixture of  claim 13  in which polymer polyol (i) is comprised of at least one solid which is a styrene/acrylonitrile mixture polymerized in situ in a polyether polyol.  
     
     
         16 . The mixture of  claim 13  in which polymer polyol (i) has from about 10 to about 60 weight percent, based on the total weight of the polymer polyol, of at least one polymer solid as a dispersed phase.  
     
     
         17 . A rigid polyurethane foam produced with the polyurethane-foam forming mixture of  claim 13 .  
     
     
         18 . The mixture of  claim 13 , wherein the foam has a density within the range of from about 5.66 to about 5.75 lbs/ft 3  and a closed-cell content of at least 80%.  
     
     
         19 . The mixture of  claim 13 , wherein the foam has a density of about 3.23 lbs/ft 3  and a closed-cell content of at least 80%.