Process for the production of highly branched Fischer-Tropsch products and potassium promoted iron catalyst

Abstract

Process for increasing the branching in products from a slurry-type Fischer-Tropsch unit by use of potassium promoted iron-based catalyst, an integrated process for increasing the yield of lubricating base oils, and an iron-based Fischer-Tropsch catalyst composition having a high atomic ratio of potassium promoter.

What is claimed is:  
     
         1 . A process for preparing a C 5  plus product with high branching from a slurry-type Fischer-Tropsch unit comprising: 
 (a) contacting a synthesis gas feed stock in a Fischer-Tropsch reaction zone with a potassium promoted iron catalyst under slurry-type Fischer-Tropsch reaction conditions, wherein the atomic ratio of iron to potassium in the catalyst is within the range of about 3 to about 15 atoms of potassium per 100 atoms of iron;    (b) recovering from the Fischer-Tropsch reaction zone a C 5  plus Fischer-Tropsch product having at least 20 mole percent branching.    
     
     
         2 . The process of  claim 1  wherein the reaction conditions in the Fischer-Tropsch reaction zone include a temperature of between about 200° C. and about 300° C., a pressure of between about 100 psig and about 400 psig and a iron catalyst space velocity between about 2 L/gr/hr and about 20 L/gr/hr.  
     
     
         3 . The process of  claim 2  wherein the reaction conditions in the Fischer-Tropsch reaction zone include a temperature of between about 210° C. and about 250° C., a pressure of between about 170 psig and about 300 psig and a iron catalyst space velocity between about 3 L/gr/hr and about 7 L/gr/hr.  
     
     
         4 . The process of  claim 1  wherein the volume ratio of hydrogen to carbon monoxide in the synthesis gas feed stock is within the range of from about 0.5 to about 2.5.  
     
     
         5 . The process of  claim 4  wherein the volume ratio of hydrogen to carbon monoxide in the synthesis gas feed stock is within the range of from about 0.5 to about 1.0.  
     
     
         6 . The process of  claim 1  wherein the atomic ratio iron to potassium in the catalyst is within the range of from about 3 and about 10 atoms of potassium to 100 atoms of iron.  
     
     
         7 . The process of  claim 1  wherein C 5  plus Fischer-Tropsch product recovered from the Fischer-Tropsch reaction zone contains less than about 5 weight percent of aromatics.  
     
     
         8 . The process of  claim 7  wherein C 5  plus Fischer-Tropsch product recovered from the Fischer-Tropsch reaction zone contains less than about 3 weight percent of aromatics.  
     
     
         9 . The process of  claim 1  wherein a product having an initial boiling point above about 340° C. is separately recovered.  
     
     
         10 . The process of  claim 9  including the additional steps of hydroisomerizing the 340° C. plus product and recovering a lube base oil.  
     
     
         11 . The process of  claim 1  wherein a diesel product is recovered from the Fischer-Tropsch reaction zone.  
     
     
         12 . The process of  claim 11  wherein the diesel product has at least 25 mole percent branching.  
     
     
         13 . The process of  claim 12  wherein the diesel product has at least 30 mole percent branching.  
     
     
         14 . The process of  claim 11  including the additional steps of contacting the diesel product with an oligomerization catalyst in an oligomerization zone under conditions selected to oligomerize the olefins in the diesel product and recovering a lube base oil product from the oligomerization zone.  
     
     
         15 . The process of  claim 1  wherein a naphtha product is recovered from the Fischer-Tropsch reaction zone.  
     
     
         16 . The process of  claim 15  including the additional steps of contacting the naphtha product with an oligomerization catalyst in an oligomerization zone under conditions selected to oligomerize the olefins in the naphtha product and recovering an oligomer product having a higher boiling point range from the oligomerization zone.  
     
     
         17 . The process of  claim 16  wherein the oligomer recovered from the oligomerization zone has an initial boiling point in excess of 340° C.  
     
     
         18 . The process of  claim 1  wherein the alpha value in the Fischer-Tropsch reaction zone is at least 0.85.  
     
     
         19 . A catalyst composition suitable for use in a slurry-type Fischer-Tropsch reactor which comprises a particulate potassium promoted iron-based catalyst wherein the atomic ratio of iron to potassium is within the range of from about 3 to about 15 atoms of potassium to 100 atoms of iron.  
     
     
         20 . The catalyst composition of  claim 19  wherein the atomic ratio of iron to potassium is with the range of from about 3 to about 10 atoms of potassium to 100 atoms of iron.  
     
     
         21 . The catalyst composition of  claim 19  wherein the atomic ratio of iron to potassium is with the range of from about 3 to about 7 atoms of potassium 100 atoms of iron.  
     
     
         22 . The catalyst composition of  claim 19  further comprising from about 1 to about 10 atoms of silicon per 100 atoms of iron.  
     
     
         23 . The catalyst composition of  claim 19  further comprising from about 0.1 to about 3 atoms of copper per 100 atoms of iron.