Copper and/or zinc alloy nanopowders made by laser vaporization and condensation

Abstract

A method of making Cu, Zn, and/or Cu/Zn alloy nanoparticles subjects one or more targets to laser energy to form a vapor and condenses the vapor to form nanoparticles having an average particle size of less than 20 nm. The optional application of an electric field results in nanoparticles with aspect ratios greater than 1.0. The target(s) can be a single target or separate targets comprising a mixture of copper, zinc, and/or copper/zinc. When separate targets are used, the laser beam can be split to form two separate beams each of which is made incident upon one of the targets. The nanoparticles can be formed in a chamber having an inert atmosphere or a reactive atmosphere and a convection current is created in the chamber by maintaining the top plate at a lower temperature than the bottom plate.

What is claimed is:  
     
         1 . A method of making nanoparticles of a copper/zinc (Cu/Zn) alloy comprising: 
 mounting one or more targets in a chamber;    vaporizing material from each of the one or more targets by subjecting each of the one or more targets to a beam of laser energy to form a vapor; and    condensing the vapor to form the Cu/Zn alloy nanoparticles.    
     
     
         2 . The method according to  claim 1 , wherein the one or more targets comprises a single target comprising a Cu/Zn alloy.  
     
     
         3 . The method according to  claim 2 , wherein the single target comprises a Cu/Zn alloy wrapped in zinc.  
     
     
         4 . The method according to  claim 2 , wherein the single target is a compact comprising copper and zinc powders or a compact comprising brass and zinc powders.  
     
     
         5 . The method according to  claim 1 , wherein the Cu/Zn alloy nanoparticles have an average particle size of less than about 20 nm.  
     
     
         6 . The method according to  claim 1 , wherein the laser is a YAG-Nd laser and wherein the emission from the laser comprises the second harmonic at a wavelength of 532 nm.  
     
     
         7 . The method according to  claim 1 , wherein the laser energy is pulsed.  
     
     
         8 . The method according to  claim 7 , wherein the pulses of laser energy have a duration of about 10 nanoseconds.  
     
     
         9 . The method according to  claim 7 , wherein each pulse of laser energy delivers from 20-40 mJ of energy to the target.  
     
     
         10 . The method according to  claim 1 , wherein the nanoparticles are formed in the presence of an electric field and wherein the nanoparticles comprise filaments, nanowires or nanotubes.  
     
     
         11 . The method according to  claim 10 , wherein the nanoparticles have an aspect ratio greater than 1.  
     
     
         12 . The method according to  claim 10 , wherein the electric field is applied at 30 to 300 V/cm.  
     
     
         13 . The method according to  claim 1 , wherein the vaporization and condensing are carried out in a diffusion cloud chamber.  
     
     
         14 . The method according to  claim 13 , wherein the diffusion cloud chamber comprises an upper portion and a lower portion and wherein the upper portion is maintained at a lower temperature than the lower portion such that the nanoparticles condense in the upper portion.  
     
     
         15 . The method according to  claim 1 , wherein an inert carrier gas or a reactive mixture comprising an inert carrier gas and a reactive gas is added to the chamber.  
     
     
         16 . The method according to  claim 15 , wherein the inert carrier gas is helium or argon.  
     
     
         17 . The method according to  claim 15 , wherein the reactive mixture comprises an inert gas and isobutene.  
     
     
         18 . The method according to  claim 15 , wherein the reactive mixture comprises oxygen and an inert gas and wherein the nanoparticles comprise one or more oxides of copper and/or zinc.  
     
     
         19 . The method according to  claim 18 , wherein the nanoparticles comprising one or more oxides of copper and/or zinc are CuO, ZnO, or Cu 2 O.  
     
     
         20 . The method according to  claim 1 , wherein the nanoparticles comprise intermetallic compounds of copper and zinc.  
     
     
         21 . The method according to  claim 20 , wherein the intermetallic compounds comprise Cu 5 Zn 8  and/or CuZn 5 .  
     
     
         22 . The method according to  claim 1 , wherein the one or more targets comprises a first target comprising copper and a second target comprising zinc, the method further comprising steps of: 
 splitting the beam of laser energy into a first beam and a second beam of laser energy;    subjecting the first target to the first beam of laser energy to form a first vapor;    subjecting the second target to the second beam of laser energy to form a second vapor;    mixing the first and second vapors; and    condensing the mixed vapors to form the Cu/Zn alloy nanoparticles.    
     
     
         23 . The method according to  claim 1 , wherein the beam of laser energy is moved relative to the one or more targets.  
     
     
         24 . The method according to  claim 1 , wherein pressure in the chamber is maintained in the range of 10 −3  to 10 −4  torr during the vaporization step.  
     
     
         25 . The method according to  claim 1 , further comprising maintaining a temperature gradient in the chamber during the vaporization step.  
     
     
         26 . The method according to  claim 1 , wherein pressure in the chamber during vaporization is maintained above atmospheric pressure.  
     
     
         27 . A method of making nanoparticles of copper (Cu) comprising: 
 mounting one or more targets in a chamber, at least one of the targets comprising a first target comprising copper;    vaporizing material from at least one of the one or more targets by subjecting the at least one target to a beam of laser energy to form a first vapor; and    condensing the first vapor to form the Cu nanoparticles.    
     
     
         28 . The method according to  claim 1 , further comprising steps of: 
 optionally mixing the first vapor and a second vapor,    wherein the second vapor is an inert carrier gas or a reactive mixture comprising an inert carrier gas and a reactive gas and the Cu nanoparticles comprise one or more oxides of copper.    
     
     
         29 . A method of making nanoparticles of zinc (Zn) comprising: 
 mounting one or more targets in a chamber, at least one of the targets comprising a first target comprising zinc;    vaporizing material from at least one of the one or more targets by subjecting the at least one target to a beam of laser energy to form a first vapor; and    condensing the first vapor to form the Zn nanoparticles.    
     
     
         30 . The method according to  claim 29 , further comprising steps of: 
 optionally mixing the first vapor and a second vapor,    wherein the second vapor is an inert carrier gas or a reactive mixture comprising an inert carrier gas and a reactive gas and the Zn nanoparticles comprise one or more oxides of zinc.    
     
     
         31 . A nanosized particle of Cu/Zn alloy having an average particle size of ≦20 nm, wherein the nanosized particle is condensed from a laser vaporized material.  
     
     
         32 . The nanosized particle of  claim 31 , wherein the average particle size is less than about 20 nm.  
     
     
         33 . The nanosized particle of  claim 31 , wherein the nanosized particles comprise one or more intermetallic compounds of copper and zinc.  
     
     
         34 . The nanosized particle of  claim 33 , wherein the intermetallic compounds comprise Cu 5 Zn 8  and/or CuZn 5 .  
     
     
         35 . A nanosized particle produced by condensation of material from a laser vaporization of first and/or second targets, wherein a first target comprises copper and a second target comprises zinc.  
     
     
         36 . The nanosized particles of  claim 35 , wherein the nanosized particles comprise one or more intermetallic compounds of copper and zinc.  
     
     
         37 . The nanosized particle of  claim 36 , wherein the intermetallic compounds comprise Cu 5 Zn 8  and/or CuZn 5 .  
     
     
         38 . A supported catalytic structure comprising: 
 a catalytic structure; and    a catalyst,    wherein the catalyst comprises a plurality of nanoparticles of Cu, Zn or Cu/Zn formed by the process of laser vaporization with controlled condensation.